Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Peridynamic Modeling of Hydrogen-Assisted White Etching Cracks in Bearing Steel under Rolling Contact Fatigue

Hydrogen-accelerated white etching area formation in bearings under rolling contact fatigue

A peridynamic damage-cumulative model for rolling contact fatigue

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

White etching area damage induced by shear localization in rolling contact fatigue of bearing steel

A peridynamic study on the effects of surface topography on rolling contact fatigue

A Study on Decisive Early Stages in White Etching Crack Formation Induced by Lubrication

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

A Peridynamic Frictional Contact Model for Contact Fatigue Crack Initiation and Propagation

Damage evolution around white etching layer during uniaxial loading

Peridynamic simulation of fatigue crack growth in porous materials

A State-Based Peridynamic Flexural Fatigue Model for Contact and Bending Conditions

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

Mechanism of fine granular area and white etching crack formation in AISI 52100 bearing steel

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

The effect of friction on surface crack initiation in rolling contact fatigue considering damage accumulation

A thermo-chemo-mechanically coupled peridynamics for investigating crack behavior in solids

Crystal plasticity modeling of grain boundary softening and fatigue in U75V pearlite steel under low strain conditions: A study of cyclic rolling contact fatigue

Modelling micropit formation in rolling contact fatigue of bearings with a crystal plasticity damage theory coupled with cohesive finite elements

Understanding Microstructure-Evolution-dependent Fracture Behaviors in Pearlitic Steels