Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

A Study on Decisive Early Stages in White Etching Crack Formation Induced by Lubrication

Development of White Etching Bands under Accelerated Rolling Contact Fatigue

White etching area damage induced by shear localization in rolling contact fatigue of bearing steel

Damage evolution around white etching layer during uniaxial loading

Peridynamic Modeling of Hydrogen-Assisted White Etching Cracks in Bearing Steel under Rolling Contact Fatigue

White Etching Bands Formation Mechanisms Due to Rolling Contact Fatigue

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Phase transformation in the subsurface of case carbonitrided bearing steels under rolling contact fatigue

Mechanism of fine granular area and white etching crack formation in AISI 52100 bearing steel

Formation Mechanism and Influence of White Etching Area on Contact Fatigue Spalling of M50 Bearing Steel

An updated review: white etching cracks (WECs) and axial cracks in wind turbine gearbox bearings

Dark etching regions under rolling contact fatigue: a review

Mechanism of White Band (WB) Formation due to Rolling Contact Fatigue in Carburized SAE4320 Steel

Fatigue Investigation on Railway Wheel Steel with White Etching Layer

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Micromechanism of cumulative damage in bearing steels under Rolling Contact Fatigue

Re‐recognition of Deep Spalling Damage Mechanism of Rolling Contact Fatigue under Heavy Load

Formation Mechanisms and Crack Propagation Behaviors of White Etching Layers and Brown Etching Layers on Raceways of Failure Bearings