Abstract:High quality silicon nitride ceramics have shown some advantages for rolling element bearing applications. In particular hybrid bearings (silicon nitride rolling elements and steel races) have the ability to withstand high loads, severe environments and high speeds. However, the difficulties of both sintering and machining the material may result in surfacedefects,such as surface ring cracks. It is difficult to detect surface ring cracks during high volume production processes and hence it is crucially important to understand their influence and the fundamental mechanism of the failures they cause. The purpose of this study is to examine the contact fatigue failure modes of silicon nitride rolling elements with surface ring crack defects. In this study, new experimental and computational techniques are developed to measure and model the interaction of the surface with pre-existing crack defects. A rolling contact fatigue test method is devised for positioning the ring crack in the contact path. Rolling contact fatigue tests are conducted using a modified four-ball machine in a hybrid ceramic/steel combination. A three-dimensional boundary element model is used to determine the stress intensity factors and to carry out the crack face contact analysis. Research shows that the RCF life performance of silicon nitride bearing elements is dependent upon the crack location and fatigue spall happens only at a few crack orientations. The spalling fatigue failure is not only influenced by the original ring crack propagation but also strongly influenced by the subsequent crack face contact. Secondary surface cracks play an important role in the forination of a fatigue spall. The crack gap and crack face friction coefficients significantly affect the formation of secondary surface cracks. Numerical calculation results are consistent with the experimental observations. A quantitative three-dimensional boundary element model has been developed, which can be used to determine the geometry of acceptable surfacering cracks.

Extended crack propagation in nitrided and carburised steels subject to rolling contact fatigue

Vertical short-crack behavior and its application in rolling contact fatigue

Rolling Contact Fatigue Crack Initiation in Medium Carbon Bainitic Steel

Rolling Contact Fatigue Failure Mechanism of Martensitic Bearing Steel after Carbonitriding

Experimental Analysis and Modelling of C-Crack Propagation in Silicon Nitride Ball Bearing Element under Rolling Contact Fatigue

Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors

Subsurface propagation of partial ring cracks under rolling contactPart II. Fracture mechanics analysis

Subsurface propagation of partial ring cracks under rolling contact: Part I. Experimental studies

Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process

Numerical analysis of rolling contact fatigue crack initiation Considering material microstructure

Failure Modes of Silicon Nitride Rolling Elements with Ring Crack Defects

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part II: Stress Modeling

Finite Element Analysis Simulation of the Effect of Induction Hardening on Rolling Contact Fatigue

BEHAVIOR OF SHORT FATIGUE CRACKS IN MEDIUM CARBON BAINITIC BACK-UP ROLL STEEL UNDER MILD TRACTIVE ROLLING CONTACT

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

The high-cycle fatigue behavior of carburized M50NiL steel with high-energy modification and compound infiltration: A comparative study

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part I: Experimental Results

Effects of carburizing and nitriding sequential treatment on rolling contact fatigue of M50NiL bearing steel

Crack Growth Behavior under Contact Fatigue of Sintered Alloy

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels