Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

BEHAVIOR OF SHORT FATIGUE CRACKS IN MEDIUM CARBON BAINITIC BACK-UP ROLL STEEL UNDER MILD TRACTIVE ROLLING CONTACT

Ratcheting led surface failure of medium carbon bainitic steel under mild operation conditions

Vertical short-crack behavior and its application in rolling contact fatigue

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

Ratcheting short crack behavior in medium carbon bainitic back-up roll steel under mild tractive rolling contact

Effect of Residual Stress Induced by Different Cooling Methods in Heat Treatment on the Fatigue Crack Propagation Behaviour of GH4169 Disc

Rolling Contact Fatigue Crack Initiation in Medium Carbon Bainitic Steel

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

Experimental Study of the Effects of Surface Defects on Rolling Contact Fatigue Behavior

Vertical Short Crack Initiation in Medium Carbon Bainitic Steel Under Mild Tractive Rolling Contact

Subsurface propagation of partial ring cracks under rolling contact: Part I. Experimental studies

The effect of friction on surface crack initiation in rolling contact fatigue considering damage accumulation

Optimization of Preventive Grinding of Backup Roll Against Contact Fatigue Cracking

On the Formation and Damage Mechanism of Rolling Contact Fatigue Surface Cracks of Wheel/rail under the Dry Condition

Subsurface propagation of partial ring cracks under rolling contactPart II. Fracture mechanics analysis

Extended crack propagation in nitrided and carburised steels subject to rolling contact fatigue

Short Fatigue-Crack Growth from Crack-like Defects under Completely Reversed Loading Predicted Based on Cyclic R-Curve

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Initiation of internal fatigue crack in a carbide-free bainitic steel during high cycle fatigue

Rail rolling contact fatigue formation and evolution with surface defects