Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Optimization of Preventive Grinding of Backup Roll Against Contact Fatigue Cracking

Ratcheting short crack behavior in medium carbon bainitic back-up roll steel under mild tractive rolling contact

Vertical Short Crack Initiation in Medium Carbon Bainitic Steel Under Mild Tractive Rolling Contact

Numerical Investigation of the Evolution of Grit Fracture and Its Impact on Cutting Performance in Single Grit Grinding

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

Vertical short-crack behavior and its application in rolling contact fatigue

Analysis and Optimization of Cvc Backup Roll Contour of A 1800mm Continuous Hot Rolling Mill

BEHAVIOR OF SHORT FATIGUE CRACKS IN MEDIUM CARBON BAINITIC BACK-UP ROLL STEEL UNDER MILD TRACTIVE ROLLING CONTACT

Finite Element Analysis of Contact Stresses on the Backup Roll of CVC Hot Rolling Mills

Ratcheting led surface failure of medium carbon bainitic steel under mild operation conditions

Rolling Contact Fatigue Crack Initiation in Medium Carbon Bainitic Steel

Subsurface propagation of partial ring cracks under rolling contact: Part I. Experimental studies

Effect of grinding parameters on surface quality, microstructure and rolling contact fatigue behaviors of gear steel for vacuum pump

The effect of friction on surface crack initiation in rolling contact fatigue considering damage accumulation

Experimental Study of the Effects of Surface Defects on Rolling Contact Fatigue Behavior

Effect of Primary Carbides on Rolling Contact Fatigue Behaviors of M50 Bearing Steel

Assessment of Surface Wear Properties with Initial Macro Crack Defects Using On-Line Visual Ferrography and Sem Methods

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Effect of Banded Carbide Structure on the Rolling Contact Fatigue of GCr15 Bearing Steel

An Investigation of the Contact Fatigue Characteristics of an RV Reducer Crankshaft, Considering the Hardness Gradients and Initial Residual Stress

Comparative Study on Surface Contact Fatigue of Machine Tool Bearing Raceways with Different Rolling Elements: Two Failure Bearings Case Studies