Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

On the Formation and Damage Mechanism of Rolling Contact Fatigue Surface Cracks of Wheel/rail under the Dry Condition

Experimental study on wheel-rail rolling contact fatigue damage starting from surface defects under various operational conditions

Rail rolling contact fatigue formation and evolution with surface defects

Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects

Evolution of microscopic characteristics of rolling contact fatigue coexisting with wear of U75V rail

Fatigue crack growth in wheel-rail rolling-sliding contact: A perspective of elastic-plastic fracture mechanics criterion

Study on wear and rolling contact fatigue behaviours of defective rail under different slip ratio and contact stress conditions

The Influence of Wheel Flats Formed from Different Braking Conditions on Rolling Contact Fatigue of Railway Wheel

Effect of Mechanical Properties of Rail and Wheel on Wear and Rolling Contact Fatigue

Experimental Investigation on the Wear and Damage Behaviors of Machined Wheel-Rail Materials under Dry Sliding Conditions

Gaps, challenges and possible solution for prediction of wheel–rail rolling contact fatigue crack initiation

Numerical investigation on wheel-rail impact contact solutions excited by rail spalling failure

Numerical simulation of rail surface-initiated rolling contact fatigue in the switch panel of railway turnouts

Analysis of fatigue crack propagation in rails under combined action of wheel load and residual stress

Rough surface rolling contact fatigue crack stress intensity factor calculation for modern rail steels

Subsurface propagation of partial ring cracks under rolling contact: Part I. Experimental studies

Study on rolling contact fatigue crack initiation and propagation in U75V rail treated by laminar plasma

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Effects of solid friction modifier on friction and rolling contact fatigue damage of wheel-rail surfaces

Investigation on wear and rolling contact fatigue of wheel-rail materials under various wheel/rail hardness ratio and creepage conditions

Wear and RCF problems of metro wheel/rail systems: Phenomena, causes and countermeasures in China