Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

The Influence of Wheel Flats Formed from Different Braking Conditions on Rolling Contact Fatigue of Railway Wheel

ANALYSIS STUDY ON BENDING FATIGUE TEST OF AUTOMOBILE WHEELS

On the Formation and Damage Mechanism of Rolling Contact Fatigue Surface Cracks of Wheel/rail under the Dry Condition

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Experimental study on wheel-rail rolling contact fatigue damage starting from surface defects under various operational conditions

Fatigue crack growth in wheel-rail rolling-sliding contact: A perspective of elastic-plastic fracture mechanics criterion

Influence of material properties on the high-speed wheel-rail rolling contact behaviour

Research on the damage mechanism of the rolling contact fatigue of a wheel–rail contact system under the influences of surface defects

Evolution of microscopic characteristics of rolling contact fatigue coexisting with wear of U75V rail

Impact of wheel profile evolution on wheel-rail dynamic interaction and surface initiated rolling contact fatigue in turnouts

Wheel wear and rolling contact fatigue evolution under interaction of abrasive block and wheel–rail contact: results from field test

Study on wear and rolling contact fatigue behaviours of defective rail under different slip ratio and contact stress conditions

Effect of Mechanical Properties of Rail and Wheel on Wear and Rolling Contact Fatigue

Effects of solid friction modifier on friction and rolling contact fatigue damage of wheel-rail surfaces

Rail rolling contact fatigue formation and evolution with surface defects

Evaluation of Thermal Fatigue Life and Crack Morphology in Brake Discs of Low-Alloy Steel for High-Speed Trains

Wear and damage transitions of two kinds of wheel materials in the rolling-sliding contact

Numerical Simulation and Mechanism Analysis of Thermal Fatigue Crack for Low-Alloy Steel Brake Disc of High-Speed Train

Wear and RCF problems of metro wheel/rail systems: Phenomena, causes and countermeasures in China

New insight on wheel flange/rail gauge lubrication: Effect of lasered microtexture shapes on the wear and fatigue behaviour of wheel/rail steels

On High Cycle Fatigue Characteristic of Locomotive Wheels