Finite Element Simulation and Fatigue Damage Analysis of High-Speed Train Gearbox Shell Based on Structure and Material Cross-Scale Correlation
Yibo Ai,Zhenwei Yang,Hongbo Que,Weidong Zhang,Ai, Yibo,Yang, Zhenwei,Que, Hongbo,Zhang, Weidong
DOI: https://doi.org/10.1007/s11668-022-01368-y
2022-05-18
Journal of Failure Analysis and Prevention
Abstract:High-speed train gearbox shell is a typical non-repairable and long-term service structure, with long design life, short service time, scarce failure data, complex structure, high test cost and non-independent test, leading tremendous difficulty to carry out the fatigue damage test and residual life prediction. In this paper, a cross-scale method of structure and material is proposed to combine the finite element analysis of structure level and stress-life analysis of material level. This method can avoid the limitation that the finite elements simulation cannot give relatively accurate result for the high-cycle fatigue, considering the S-N curve is suitable for the high-cycle fatigue life prediction. Though it is not easy to carry out damage test for the structure of high-speed train gearbox shell, the structure numerical simulation result and materials fatigue test result can be combined to estimate the remaining life of high-speed train gearbox shell and give out the relatively accurate result. According to the cross-scale correlation strategy of structure and material, the most vulnerable part is located at the part with the maximum stress. The S-N curve of the shell material under different stresses was obtained using material fatigue test, and the life cycles of the high-speed train gearbox shell deduced by S-N curve is 87.000.000 km under 20.65MPa stress, which is corresponding with the design life expected by shell manufacture.