Abstract:The connection between the cleanliness of 52100 type bearing steels and their reliability has been well documented. Most research over the past 30 years has focused on sensitive compositional control during metallurgical refinement, leading to steels so clean that industrial cleanness standards are no longer suitable for quantifying further improvements. There is less literature, however, detailing the mechanism by which different impurities initiate rolling contact fatigue (RCF). Early work focused on comparing fatigue lives with cleanness ratings, which include a worst field analysis to determine the inclusion content and post-failure analysis to determine damage nucleation sites. The stress concentrations around discontinuities in the steel matrix can now however be visualised using computational modelling techniques. There is now a much clearer picture of how non-metallic inclusions (NMIs) nucleate fatigue damage by causing changes in the subsurface microstructure, including white etching regions in the form of butterflies. Size, morphology, distribution and type of inclusion are important factors for determining their role in RCF and the ability to control these variables could lead to improved performance. The inclusion character is greatly influenced by the steelmaking process, from initial melt through to casting, as well as hot deformation. While the impact of microchemical banding on RCF is not well understood, the effect of microsegregation on the phases that form can be modelled using simple calculations. Hot rolling techniques also influence the steel cleanliness, as NMIs can be plastically deformed or broken up and voids can be introduced around them, thus affecting the interface with the matrix. Understanding the microstructure evolution from materials characterisation and the ability to model the process could establish an optimum degree of rolling reduction. This could greatly aid the production of large bearings, as some manufacturers currently make them from very large ingots to achieve the necessary reduction ratio and therefore required level of performance.

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part II: Stress Modeling

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part I: Experimental Results

Rolling Contact Fatigue Life and Spall Propagation Characteristics of AISI M50, M50 NiL, and AISI 52100, Part III: Metallurgical Examination

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Influence of Residual Stress and Temperature on the Cyclic Hardening Response of M50 High-Strength Bearing Steel Subjected to Rolling Contact Fatigue

Investigation into Rolling Contact Fatigue Performance of Aerospace Bearing Steels

Effect of spatial hardness distribution in rolling contact fatigue performance of bearing contacts

Extended crack propagation in nitrided and carburised steels subject to rolling contact fatigue

Cyclic Constitutive Response and Effective S–N Diagram of M50 NiL Case-Hardened Bearing Steel Subjected to Rolling Contact Fatigue

On the effect of microplasticity on crack initiation from subsurface defects in rolling contact fatigue

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Subsurface propagation of partial ring cracks under rolling contact: Part I. Experimental studies

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

Experimental Study of the Effects of Surface Defects on Rolling Contact Fatigue Behavior

Finite Element Analysis Simulation of the Effect of Induction Hardening on Rolling Contact Fatigue

Investigation on Rolling Contact Fatigue of 55 Medium-Carbon Steel

Study of the Plastic Behavior of Rough Bearing Surfaces Using a Half-Space Contact Model and the Fatigue Life Estimation According to the Fatemi–Socie Model

Improving the reliability of highly loaded rolling bearings: the effect of upstream processing on inclusions

Numerical analysis of rolling contact fatigue crack initiation Considering material microstructure

Experimental investigations to assess surface fatigue failure in rolling contact bearing