Abstract:In this investigation the effect of various spatial hardness gradients (e.g. linear and nonlinear) on rolling contact fatigue (RCF) life are examined through a Mises-based plasticity framework. The plasticity framework, which utilizes kinematic hardening was embedded into a finite element (FE) model, which utilized continuum damage mechanics (CDM) to facilitate life calculations by simulating material deterioration as a function of cycle. CDM critical parameters – elastic damage law resistance stress (σr), elastic damage rate exponent (m), plastic damage law resistance stress (S0), plastic damage rate exponent (q) – were established from open literature experimental torsion stress-life data. A parametric study was then performed to quantify the relation between RCF life and (1) type of spatial gradient (e.g. linear, polynomial degree 4, polynomial degree 0.25), (2) depth of spatial gradient normalized with respect to half-contact width (e.g. 1b, 2.5b, 5b, 10b), (3) magnitude of residual stress, and (4) contact pressure. Additionally, FE simulations were conducted on non-graded, or uniform hardness microstructures and used to compare to the results from the parametric study. The RCF results indicated that polynomial gradients with degree greater than 1 outperform linear and polynomial gradients with degree less than 1, with differences between gradient types more apparent at shallower gradient depths. RCF resistance is improved with increasing gradient depth and increasing compressive residual stress. Regression analysis of the results from this investigation yielded a fatigue life expression that was formed as a function of the 4 input variables, with life improvement factors comparing well with experimental data from the open literature.

Influence of Residual Stress and Temperature on the Cyclic Hardening Response of M50 High-Strength Bearing Steel Subjected to Rolling Contact Fatigue

Cyclic Constitutive Response and Effective S–N Diagram of M50 NiL Case-Hardened Bearing Steel Subjected to Rolling Contact Fatigue

Work hardening response of M50-NiL case hardened bearing steel during shakedown in rolling contact fatigue

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Effects of carburizing and nitriding sequential treatment on rolling contact fatigue of M50NiL bearing steel

Effect of Primary Carbides on Rolling Contact Fatigue Behaviors of M50 Bearing Steel

Finite Element Analysis Simulation of the Effect of Induction Hardening on Rolling Contact Fatigue

Microstructure–Property Relationships in M50-NiL and P675 Case-Hardened Bearing Steels

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

The Performance of 52100, M-50, and M-50 NiL Steels in Radial Bearings

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part I: Experimental Results

Prediction of Work Hardening in Bearing Steels Undergoing Rolling Contact Loading with a Dislocation-Based Model

Micromechanical response of dual-hardening martensitic bearing steel before and after rolling contact fatigue

Rolling Contact Fatigue Life and Spall Propagation of AISI M50, M50NiL, and AISI 52100, Part II: Stress Modeling

A Rolling Contact Fatigue Study of Hard Carbon Coated M-50 Steel

Experimental Study of the Effects of Surface Defects on Rolling Contact Fatigue Behavior

Effect of spatial hardness distribution in rolling contact fatigue performance of bearing contacts

Relating rolling contact fatigue (RCF) life to the microstructure evolution in aerospace grade bearing steels: A comparison of Cronidur-30 with AISI 440C