Abstract:M50 bearing steel has great potential for applications in the field of aerospace engineering, as it exhibits outstanding mechanical and physical properties. From a microscopic point of view, bearing wear originates from the microscopic region of the contact interface, which usually only contains hundreds or even several atomic layers. However, the existing researches seldom study the wear of M50 bearing steel on the microscopic scale. This study explored the atomic-scale modeling method of M50 bearing steel. Then molecular dynamics simulations of nanoindentation on the M50 bearing steel model were carried out to study the size effect of the mechanical behaviors. The simulation results show that with the change in the radius of the diamond indenter in the nanoindentation simulation, the calculated nanohardness decreases. According to the size effect, when the indentation radius is 200 nm, the hardness obtained by the simulation is about 9.26 GPa, and that of the M50 sample measured by the nanoindentation is 10.4 GPa. Then nanoindentation simulations were carried out at different temperatures. The main bearings of aero-engines generally work at 300–500 degrees Celsius. When the simulated temperature was increased from 300 K to 800 K, the hardness of the model decreased by 15%, and the model was more prone to plastic deformation. In this study, a new molecular dynamics modeling method for M50 bearing steel was proposed, and then nanoindentation simulation was carried out, and the nanoindentation experiment verified the correctness of the model. These results are beneficial to the basic understanding of the mechanical performance of M50 bearing steel.

Work hardening response of M50-NiL case hardened bearing steel during shakedown in rolling contact fatigue

Influence of Residual Stress and Temperature on the Cyclic Hardening Response of M50 High-Strength Bearing Steel Subjected to Rolling Contact Fatigue

Cyclic Constitutive Response and Effective S–N Diagram of M50 NiL Case-Hardened Bearing Steel Subjected to Rolling Contact Fatigue

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

A Rolling Contact Fatigue Study of Hard Carbon Coated M-50 Steel

Prediction of Work Hardening in Bearing Steels Undergoing Rolling Contact Loading with a Dislocation-Based Model

Finite Element Analysis Simulation of the Effect of Induction Hardening on Rolling Contact Fatigue

Approach to investigate pre-nucleation fatigue damage of cyclically loaded metals using Vickers microhardness tests

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Microstructure–Property Relationships in M50-NiL and P675 Case-Hardened Bearing Steels

Effects of carburizing and nitriding sequential treatment on rolling contact fatigue of M50NiL bearing steel

Effect of Primary Carbides on Rolling Contact Fatigue Behaviors of M50 Bearing Steel

Experimental Study of the Effects of Surface Defects on Rolling Contact Fatigue Behavior

The high-cycle fatigue behavior of carburized M50NiL steel with high-energy modification and compound infiltration: A comparative study

The Performance of 52100, M-50, and M-50 NiL Steels in Radial Bearings

Micromechanical response of dual-hardening martensitic bearing steel before and after rolling contact fatigue

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Rolling contact fatigue behaviour of M50 bearing steel with rare earth addition

Molecular Dynamics Simulation on Nanoindentation of M50 Bearing Steel