Abstract:During the bearing service, a series of microstructural evolutions will arise inside the material, such as the appearance of feature microstructures. The essential reason for the microstructural evolution is the cumulative effect of cyclic stress. The Hertz Contact formula is usually adopted to calculate the internal stress, and there is a correlation between the shape and distribution of the feature microstructure and the stress distribution. But it is insufficient to explain the relationship between the morphology of feature microstructures and the rolling direction, such as specific angles in butterfly and white etching bands. The rolling phenomenon will cause the asymmetry of stress distribution in the material, which is the source of the rolling friction coefficient. Moreover, slipping or microslip will produce additional stress components, which also cause the asymmetry of the stress field. However, there is no experimental or theoretical explanation for the relationship between the asymmetry of the stress field and the feature microstructure. According to the current theory, the appearance of feature microstructures is caused by stress with or without rolling. Therefore, it is of great significance to study the formation mechanism: whether feature microstructures will appear in the uniaxial cyclic compression stress field without rolling. In this paper, uniaxial cyclic compressive stress was loaded into a plate-ball system and a cylinder system. The characteristics of microstructural change of bearing steel (GCr15) were studied. It was found that the hardness of the material increased after the cyclic compressive load, and the inclusions interacted with the matrix material. In the local microregion a white etching area was found, although the scale is very small. No large-scale feature microstructures appeared. Other phenomena in the experiment are also described and analyzed. For example, the production of oil film in the contact area and the changing law of alternating load.

A study of local microstructure decay in GCr15 due to rolling contact

Preliminary Research on Response of GCr15 Bearing Steel under Cyclic Compression

Microstructure Evolution in GH4169 Alloy during Cross-Wedge Rolling

Fatigue and recrystallization evolution of carbide-free bainitic layer under high-stress rolling sliding contact

Micromechanical response of dual-hardening martensitic bearing steel before and after rolling contact fatigue

Microstructure Evolution of a Hypereutectoid Pearlite Steel under Rolling-Sliding Contact Loading

Atomic-Scale Insights into Damage Mechanisms of GGr15 Bearing Steel Under Cyclic Shear Fatigue

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Enhanced surface properties and contact fatigue performance of Cr4Mo4V bearing steel subjected to ultrasonic surface rolling processingVerbesserte Oberflacheneigenschaften und Kontaktermudungsleistung von einem ultraschall-oberflachengewalzten Cr4Mo4V-Lagerstahl

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

On the microstructure evolution and nanocrystalline formation of pearlitic wheel material in a rolling-sliding contact

The Effect of Cold Ring Rolling on the Heat Treatment Microstructure and Wear Resistance of GCr15 Bearing Steel

Microstructure Alterations and White Etching Area Formation in Bearing Steels under High-Frequency Dynamic Loading

Failure analysis for outer ring cracking of GCr15 rolling bearing

Effect of Hot Rolling on Microstructural Evolution and Wear Behaviors of G20CrNi2MoA Bearing Steel

Numerical analysis of rolling contact fatigue crack initiation Considering material microstructure

Surface Microstructure Refinement and Mechanical Properties of GCr15 Steels Improved During Ultrasonic Surface Rolling Processing

An electron backscatter diffraction investigation on microstructural evolution of pearlite wheel steel near rolling contact fatigue crack tip

Vertical short-crack behavior and its application in rolling contact fatigue

Ratcheting short crack behavior in medium carbon bainitic back-up roll steel under mild tractive rolling contact