Abstract:During the bearing service, a series of microstructural evolutions will arise inside the material, such as the appearance of feature microstructures. The essential reason for the microstructural evolution is the cumulative effect of cyclic stress. The Hertz Contact formula is usually adopted to calculate the internal stress, and there is a correlation between the shape and distribution of the feature microstructure and the stress distribution. But it is insufficient to explain the relationship between the morphology of feature microstructures and the rolling direction, such as specific angles in butterfly and white etching bands. The rolling phenomenon will cause the asymmetry of stress distribution in the material, which is the source of the rolling friction coefficient. Moreover, slipping or microslip will produce additional stress components, which also cause the asymmetry of the stress field. However, there is no experimental or theoretical explanation for the relationship between the asymmetry of the stress field and the feature microstructure. According to the current theory, the appearance of feature microstructures is caused by stress with or without rolling. Therefore, it is of great significance to study the formation mechanism: whether feature microstructures will appear in the uniaxial cyclic compression stress field without rolling. In this paper, uniaxial cyclic compressive stress was loaded into a plate-ball system and a cylinder system. The characteristics of microstructural change of bearing steel (GCr15) were studied. It was found that the hardness of the material increased after the cyclic compressive load, and the inclusions interacted with the matrix material. In the local microregion a white etching area was found, although the scale is very small. No large-scale feature microstructures appeared. Other phenomena in the experiment are also described and analyzed. For example, the production of oil film in the contact area and the changing law of alternating load.

Microstructure Evolution of a Hypereutectoid Pearlite Steel under Rolling-Sliding Contact Loading

On the microstructure evolution and nanocrystalline formation of pearlitic wheel material in a rolling-sliding contact

Phase and Microstructural Evolution in White Etching Layer of a Pearlitic Steel During Rolling–sliding Friction

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Understanding Cementite Dissolution in Pearlitic Steels Subjected to Rolling-Sliding Contact Loading: A Combined Experimental and Theoretical Study

Fatigue and recrystallization evolution of carbide-free bainitic layer under high-stress rolling sliding contact

An Investigation of Friction Coefficient on Microstructure and Texture Evolution of Interstitial-Free Steel during Warm Rolling and Subsequent Annealing

Investigation on Rolling Contact Fatigue of 55 Medium-Carbon Steel

An electron backscatter diffraction investigation on microstructural evolution of pearlite wheel steel near rolling contact fatigue crack tip

A study of local microstructure decay in GCr15 due to rolling contact

Understanding Microstructure-Evolution-dependent Fracture Behaviors in Pearlitic Steels

Preliminary Research on Response of GCr15 Bearing Steel under Cyclic Compression

Microstructure evolution and deformation mechanism of coherent L12-strengthened high-entropy alloy during sliding wear

Microstructure Evolution in GH4169 Alloy during Cross-Wedge Rolling

New insight into the dry rolling-sliding wear mechanism of carbide-free bainitic and pearlitic steel

Microstructure Alterations and White Etching Area Formation in Bearing Steels under High-Frequency Dynamic Loading

Comparison of the damage and microstructure evolution of eutectoid and hypereutectoid rail steels under a rolling-sliding contact

Phase transformation in the subsurface of case carbonitrided bearing steels under rolling contact fatigue

Microstructure and Texture Evolution of Cu-Ni-P Alloy after Cold Rolling and Annealing

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue