Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

An electron backscatter diffraction investigation on microstructural evolution of pearlite wheel steel near rolling contact fatigue crack tip

On the microstructure evolution and nanocrystalline formation of pearlitic wheel material in a rolling-sliding contact

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Crystal plasticity modeling of grain boundary softening and fatigue in U75V pearlite steel under low strain conditions: A study of cyclic rolling contact fatigue

Influence of original microstructure on rolling contact fatigue property of D2 wheel steel

EBSD Study on Proeutectoid Ferrite and Eutectoid Ferrite Refinement Mechanism of D2 Wheel Steel Under a Rolling Condition

Understanding Microstructure-Evolution-dependent Fracture Behaviors in Pearlitic Steels

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

Phase transformation in the subsurface of case carbonitrided bearing steels under rolling contact fatigue

Microstructure Evolution of a Hypereutectoid Pearlite Steel under Rolling-Sliding Contact Loading

Phase and Microstructural Evolution in White Etching Layer of a Pearlitic Steel During Rolling–sliding Friction

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

Microstructural Dependence of Anisotropic Fracture Mechanisms in Cold-Drawn Pearlitic Steels

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

Modelling micropit formation in rolling contact fatigue of bearings with a crystal plasticity damage theory coupled with cohesive finite elements

An Investigation of Friction Coefficient on Microstructure and Texture Evolution of Interstitial-Free Steel during Warm Rolling and Subsequent Annealing

Understanding Cementite Dissolution in Pearlitic Steels Subjected to Rolling-Sliding Contact Loading: A Combined Experimental and Theoretical Study

Microstructure evolution and very-high-cycle fatigue crack initiation behavior of a structural steel with two loading intermittence modes