Abstract:The purpose of induction-heating-assisted ultrasonic surface rolling process is to introduce the temperature field into the ultrasonic surface strengthening process of materials and use the influence of heating temperature on the mechanical properties and microstructure of the material so that a surface-modified layer with improved performance can be obtained. Many studies on the ultrasonic surface rolling process have been conducted at room temperature. In this study, the effect of temperature on the surface integrity of carburised 18CrNiMo7-6 steel after ultrasonic surface rolling process was studied by induction heating. Compared with the result of ultrasonic surface rolling process at room temperature, below 250 °C, with the increase of heating temperature, the residual compressive stress and residual compressive stress depth of the sample increase continuously. The maximum surface residual compressive stress and residual compressive stress depth can be obtained at 250 °C, the surface residual compressive stress increases by 29%, and the residual compressive stress depth increases from 1700 to 2450 μm. The surface hardness of the sample also shows an increasing trend when the heating temperature is from 100 to 250 °C, and the hardness influence layer increases with the increase of heating temperature. The minimum surface roughness can be obtained by ultrasonic surface rolling process at 100 °C. In addition, the induction-heating-assisted ultrasonic surface rolling process parameters are optimised by grey correlation analysis method, and the optimum process parameters to achieve the best surface integrity are obtained as follows: static pressure of 400 N, rotation speed of 50 r/min, feed rate of 0.04 mm/r, and heating temperature of 250 °C. The order of significance of influence on surface integrity is static pressure >$$>$$ rotation speed >$$>$$ feed rate >$$>$$ heating temperature. The conclusion has a certain guiding significance for the anti-fatigue manufacturing of materials.

Enhanced surface properties and contact fatigue performance of Cr4Mo4V bearing steel subjected to ultrasonic surface rolling processingVerbesserte Oberflacheneigenschaften und Kontaktermudungsleistung von einem ultraschall-oberflachengewalzten Cr4Mo4V-Lagerstahl

Experimental study on surface integrity and fatigue life of an ultra-high strength steel by the composite strengthening process of pre-torsion and ultrasonic rolling

Microstructural evolution and surface integrity of ultrasonic surface rolling in Ti6Al4V alloy

Surface integrity and rolling contact fatigue behavior of 18CrNiMo7-6 steel subjected to ultrasonic surface rolling process

Surface Microstructure Refinement and Mechanical Properties of GCr15 Steels Improved During Ultrasonic Surface Rolling Processing

Study on microstructure of 42CrMo steel by ultrasonic surface rolling process

Study on Surface Integrity and Fatigue Properties of TC4 Titanium Alloy by Surface Ultrasonic Rolling

Effects of ultrasonic surface rolling process on tribological behavior of 4Cr13 stainless steel

Investigation on surface integrity and process parameter optimisation of carburised 18CrNiMo7-6 steel by induction-heating-assisted ultrasonic surface rolling process

Frictional Wear and Thermal Fatigue Properties of Die Steel after Ultrasound-Assisted Alloying

Fatigue and recrystallization evolution of carbide-free bainitic layer under high-stress rolling sliding contact

Effects of Surface Defects on Rolling Contact Fatigue in 10Cr4ni4mo4v

Rolling contact fatigue behaviors of 25CrNi2MoV steel combined treated by discrete laser surface hardening and ultrasonic surface rolling

Microstructure and tribological performances of M50 bearing steel processed by ultrasonic surface rolling

Effect of Ultrasonic Rolling on Surface Properties of GCr15 Spherical Joint Bearing

Experimental study on surface integrity of ultra-high-strength steel by ultrasonic hot rolling surface strengthening

Simulation study of turning-ultrasonic rolling compound processing for 42CrMo steel

Microstructures and rolling contact fatigue behaviors of 17Cr2Ni2MoVNb steel under combined ultrasonic surface rolling and shot peening

Improved fretting fatigue mechanism of surface-strengthened Ti-6Al-4V alloy induced by ultrasonic surface rolling process

Effect of ultrasonic rolling on the surface integrity and corrosion properties of GCr15 steel before and after quenching

Surface textures fabricated by laser and ultrasonic rolling for improving tribological properties of TiAlSiN coatings