Abstract:The M50 steel is a common material for main shaft bearings in aerospace applications. The thermal stability of gradient ultrafine grains/nanograins steels is of critical importance for engineering applications. Here, we fabricated gradient nanostructured M50 steel using ultrasonic shot peening and subsequent annealing. This study investigated the effect of annealing treatment on the microstructure evolution of gradient nanostructured M50 steel and the thermal stability of the USPed sample post-annealing. Furthermore, the friction behavior of gradient nanostructured M50 steel was also examined. After annealing at 350 °C for 30 min, ferrite phase at the depth span of 0–100 μm has better thermal stability, and formed a high-density dislocation network and cells at the top surface of the gradient layer. When annealed samples were continued annealed at 350 °C for 100 h, the average ferrite phase size at the depth span of 0–100 μm reduced to a fixed value (∼434 nm). High-density dislocation cells with smaller and more dispersed ordered B2 phases have a stronger pinning effect of dislocation. Hetero-deformation induced hardening by a dislocation network of grain interior and dislocation wall (∼200 nm thick) and precipitation hardening of dislocation cells with more dispersed ordered B2 phase is the main reason for the high microhardness of the samples annealing at 350 and 450 °C for 30 min. The USPed sample within the 100–200 μm depth span exhibits better friction properties attributed to the strengthened martensitic matrix, partial decomposition of spherical carbides, and the presence of high-density dislocations, which reduce the cracking of carbides and matrix, and carbide spalling. Although heat treatment results in a slight decrease in the friction properties of the USPed sample, they still surpass those of the tempered sample. This reduction in friction properties post-annealing primarily arises from the annihilation of high-density dislocations.

Microstructure and tribological performances of M50 bearing steel processed by ultrasonic surface rolling

Surface Microstructure Refinement and Mechanical Properties of GCr15 Steels Improved During Ultrasonic Surface Rolling Processing

Study on microstructure of 42CrMo steel by ultrasonic surface rolling process

Enhanced Wear Resistance of the Ultrastrong Ultrasonic Shot-Peened M50 Bearing Steel with Gradient Nanograins

Effect of Ultrasonic Rolling on Surface Properties of GCr15 Spherical Joint Bearing

Understanding the thermal stability and friction behavior of ultrasonic shot peening-introduced gradient nanostructured M50 bearing steel

Effect of corrosion on the fatigue damage behavior of M50 steel treated by ultrasonic surface rolling process

Effects of ultrasonic surface rolling process on tribological behavior of 4Cr13 stainless steel

Enhanced surface properties and contact fatigue performance of Cr4Mo4V bearing steel subjected to ultrasonic surface rolling processingVerbesserte Oberflacheneigenschaften und Kontaktermudungsleistung von einem ultraschall-oberflachengewalzten Cr4Mo4V-Lagerstahl

Surface integrity and rolling contact fatigue behavior of 18CrNiMo7-6 steel subjected to ultrasonic surface rolling process

Exploration of Key Process Parameters and Properties of 40Cr Steel in Ultrasonic Surface Rolling Process

Effect of Ultrasonic Surface Rolling on the Microstructure and Corrosion Properties of Gear Steel 20CrNiMo After Carburizing

Improved wear resistance of 440 C steel ball via ultrasonic strengthening grinding process

Optimizing tribological property by inducing the gradient microstructure and surface topography in martensite stainless steel

Microstructures and mechanical properties of Mg-15Gd-1Zn-0.4Zr alloys treated by ultrasonic surface rolling process

Effect of ultrasonic surface rolling process on the surface properties of QAl10-3-1.5 aluminum bronze alloy

Athermally induced MC carbide decomposition in gradient M50 bearing steels during electric pulse treatments

Study on Fretting Wear Properties of GCr15 Steel Via Ultrasonic Surface Rolling Process

Bending Fatigue Behaviour and Fatigue Endurance Limit Prediction of 20Cr2Ni4A Gear Steel after the Ultrasonic Surface Rolling Process

Effect of ultrasonic surface rolling on surface layer properties and fretting wear properties of titanium alloy Ti5Al4Mo6V2Nb1Fe

Effect of ultrasonic surface rolling on the friction and wear properties of 8620H carburized steel at elevated temperatures