Abstract:The powders produced by plasma-arc wire atomization in an argon atmosphere or air were studied for their use in 3D printing of complex-shaped metal parts and in granular metallurgy. The dependence of the morphology, structure, phase composition, and microhardness of the powders on the current and atomization conditions was established. In all studied operating modes of the plasma torch (180, 220, and 270 A), the atomized particles are predominantly spherical. The number of nonspherical particles increases with particle size. The powders atomized in an argon atmosphere exhibit a stable phase composition. The main component is iron aluminide Fe 3 Al (or a mixture of Fe 3 Al and AlFe). The α-Fe, Fe 3 O 4 , and Fe 2 O 3 phases were also found. At currents of 220 and 270 A, the powder in –200+100 μm fraction contains the highest amount of aluminides, 83.88 and 86.30 wt.%, and the lowest content of oxides, 6.61–10.18 wt.%. In fine powders (–100+75 μm), the content of aluminides is 70.38– 28.3 wt.%), but the amount of oxides increases to 23.32–29.62 wt.%. The microhardness of oxide particles (5320–8150 MPa) is higher than that of metal particles (3070–4590 MPa). In atomization in air, the key components are Fe 2 O 3 , Fe 3 O 4 , FeO, and Al 3 O 4 . The total amount of oxides reaches 57.19–90.34%. The percentage of iron aluminides decreases significantly, and their maximum content (28.3 wt.%) is shown by the –315+200 μm powder at a plasma torch current of 270 A. In the finest powder fraction of –100+75 μm, the content of aluminides ranges from 6.2 to 15.36 wt.%. The average microhardness of metal particles is much lower (2750–4940 MPa) than that of oxide particles (4500–7460 MPa). It was found that the best material in terms of phase composition, structure, hardness, and shape factor was produced by atomization of a flux-cored wire in an argon atmosphere. In atomization in air, intense oxidation processes occur.

Plasma way to obtain ultrafine iron and aluminum oxides

Recent Progresses in Material Fabrication and Modification by Cold Plasma Technique

Study of the Possibility of Using an Alternating Current Plasma Torch to Obtain Ultrafine Tungsten Carbide

Low-Temperature Underwater Plasma as an Instrument to Manufacture Inorganic Nanomaterials

A stable atmospheric-pressure plasma for extreme-temperature synthesis

Study of the properties of metal powder received by plasma

Direct Production of Ultrafine Amorphous Fe-P Alloy Particles by the Plasma Method

Plasma Processing of Iron Ore

Modeling and Selection of RF Thermal Plasma Hot-Wall Torch for Large-Scale Production of Nanopowders

Synthesis of Functional Nanoassemblies in Reactive Plasmas

Oxide Reduction Treatment with a Thermal Plasma Torch: A Case Study

Properties of Powders Produced by Plasma-Arc Spheroidization of Current-Carrying Fe–Al Flux-Cored Wire

Production Silicon Carbide Based on Micro and Nano-Sized Silicon Dioxide in Conditions of Thermal Plasma Energy

Technology for High Pure Aluminum Oxide Production from Aluminum Scrap

Gas Phase Chemical Evolution of Uranium, Aluminum, and Iron Oxides

Plasma for Rapid Conversion Reactions and Surface Modification of Electrode Materials

A New Method to Produce Superfine and Nano-Sized Fe Powders: Spark Plasma Discharge Process

Synthesis of Ultra-Fine Iron Powder by Combining the Flame Aerosol Synthesis and Postreduction

Towards large-scale plasma-assisted synthesis of nanowires

Investigation of Plasma-Chemical Synthesis of Complex Oxide Compositions for Dispersed Uranium-Plutonium Mixed Fuel

Synthesis of nanostructured materials by hot and cold plasma