Abstract:The powders produced by plasma-arc wire atomization in an argon atmosphere or air were studied for their use in 3D printing of complex-shaped metal parts and in granular metallurgy. The dependence of the morphology, structure, phase composition, and microhardness of the powders on the current and atomization conditions was established. In all studied operating modes of the plasma torch (180, 220, and 270 A), the atomized particles are predominantly spherical. The number of nonspherical particles increases with particle size. The powders atomized in an argon atmosphere exhibit a stable phase composition. The main component is iron aluminide Fe 3 Al (or a mixture of Fe 3 Al and AlFe). The α-Fe, Fe 3 O 4 , and Fe 2 O 3 phases were also found. At currents of 220 and 270 A, the powder in –200+100 μm fraction contains the highest amount of aluminides, 83.88 and 86.30 wt.%, and the lowest content of oxides, 6.61–10.18 wt.%. In fine powders (–100+75 μm), the content of aluminides is 70.38– 28.3 wt.%), but the amount of oxides increases to 23.32–29.62 wt.%. The microhardness of oxide particles (5320–8150 MPa) is higher than that of metal particles (3070–4590 MPa). In atomization in air, the key components are Fe 2 O 3 , Fe 3 O 4 , FeO, and Al 3 O 4 . The total amount of oxides reaches 57.19–90.34%. The percentage of iron aluminides decreases significantly, and their maximum content (28.3 wt.%) is shown by the –315+200 μm powder at a plasma torch current of 270 A. In the finest powder fraction of –100+75 μm, the content of aluminides ranges from 6.2 to 15.36 wt.%. The average microhardness of metal particles is much lower (2750–4940 MPa) than that of oxide particles (4500–7460 MPa). It was found that the best material in terms of phase composition, structure, hardness, and shape factor was produced by atomization of a flux-cored wire in an argon atmosphere. In atomization in air, intense oxidation processes occur.

Direct Production of Ultrafine Amorphous Fe-P Alloy Particles by the Plasma Method

Fe-P-B Ultrafine Amorphous Particles Produced by Chemical Reduction

Chemical Preparation and Investigation of Fe-P-B Ultrafine Amorphous Alloy Particles

Investigation of Amorphous Fe82P11B7ultrafine Particles Produced by Chemical Reduction

Properties of Powders Produced by Plasma-Arc Spheroidization of Current-Carrying Fe–Al Flux-Cored Wire

Clean production of Fe-based amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore and apatite

Determining the Composite Structure of Au-Fe-Based Submicrometre Spherical Particles Fabricated by Pulsed-Laser Melting in Liquid

Effect of bath temperature on electrodeposition behaviour and corrosion properties of amorphous Fe–P alloys obtained from additive-free chloride baths

Effects of spark plasma sintering parameters on properties of Fe-based bulk amorphous alloys

General route to fabricate ultrafine metallic glass powders directly from their own crystalline states by localized pulsed electrical discharge atomization

Research of Superfine Fe Powder Prepared by Spark Plasma Erosion

Synthesis of Fe-Al Nanoparticles by Hydrogen Plasma-Metal Reaction

Ultrafine Amorphous Fe-Ni-B And Fe-P-B Particles

Production of Spheroidized Micropowders of W-Ni-Fe Pseudo-Alloy Using Plasma Technology

Plasma way to obtain ultrafine iron and aluminum oxides

A New Method to Produce Superfine and Nano-Sized Fe Powders: Spark Plasma Discharge Process

Properties of Ultrafine Amorphous Fe-Ni-B Powder Produced by Chemical-Reduction

Spherical amorphous nickel-phosphorus alloy particles with uniform size prepared at room temperature

Investigation on close-coupled gas atomization for Fe-based amorphous powder production via simulation and industrial trials: Part II. Particle flight and cooling during secondary atomization

Investigation on the Controllable Microstructures of High Iron Content Al–Fe Alloys Fabricated Via Solid–Liquid Mixture Method Combining with Plasma Arc Heating Approach

Plasma electrolytic fluorination on Al alloys: Coating growth and plasma discharge behavior