Abstract:To realize cost-effectively manufacture of high-performance Si3N4 porous ceramic, a ferrosilicon nitride porous ceramic with an optimized interlocking structure was synthesized by flash combustion synthesis using FeSi75 powder as raw material. And the technology has been improved in many ways to ensure stable industrial production. The theoretical combustion temperature of FeSi75 in N2(g) is up to 4608K, while Si3N4 is unstable. Both adding diluent and designing the preheat temperature of nitrogen are taken to control synthesis temperature below 1600 °C. During synthesis, the Fe–Si liquid phase and SiO(g), which are essential for the selective growth of elongated columnar β-Si3N4 and whisker α-Si3N4 respectively, are formed firstly. Then, nitriding proceed in multiple ways. N diffuses through Fe–Si(l) and reacts with Si to form β-Si3N4, and the growth of elongated β-Si3N4 in Fe–Si liquid follows the dynamic ripening model, which is very fast and effective. Thus, an interlocking structure composed of elongated β-Si3N4 with an aspect ratio above 20 is reached. There is also an indirect nitridation reaction, that is, FeSi75 preferentially reacts with trace O2 in atmosphere to form SiO(g), which is further nitrided to form needle-like α-Si3N4. Needle-like α-Si3N4 is interspersed in the well-developed columnar β-Si3N4, making the structure stronger. Fe finally exists in the form of Fe3Si, which binds the surrounding elongated Si3N4 to form a sea-urchin like unit, making the structure more stable and strengthened. Through control of these reactions, optimizations in microstructure are reached, and the annual output of has reached 25,000 tons. The reaction model is established.

Preparation method for producing high purity beta-phase silicon nitride by combustion synthesis method

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Research of Silicon Nitride Powder Prepared by Self-propagating High-temperature Synthesis

Preparation of silicon nitride powder from silica and ammonia

Preparation of high‐purity α‐Si3N4 powder via multifunctional synergistic catalysis and pretreatment method

Cost-effective manufacture and synthesis mechanism of ferrosilicon nitride porous ceramic with interlocking structure

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Effect of the Diluent on Combustion Synthesis of Silicon Nitride

Effect of nitrogen pressure on combustion synthesis of Si3N4-SiC-TiN ceramic

Combustion synthesis of fine aluminum nitride powders under micropositive N 2 pressure with water additive

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

Preparation of silicon nitride fibers by additive-assisted nitridation of polysilicon waste powder

Efficient Preparation of Si3N4 by Microwave Treatment of Solar-Grade Waste Silicon Powder

Controllable Synthesis Of High-Purity Beta-Sialon Powder

Study on rapid nitridation process of molten silicon by thermogravimetry and in‐situ Raman spectroscopy

Silicon vanadium nitride microalloy and preparation method thereof

Controllable Synthesis of High-purity β-SiAlON Powder

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production