Influence of temperature on hot corrosion behavior of GH4169 superalloy subjected to Na 2 SO 4 -NaCl salts attack
Baishun Yang,Biao Li,Xiaoxiao Chen,Yaning Zhang,Yazhi Li
DOI: https://doi.org/10.1016/j.matchemphys.2024.129731
IF: 4.778
2024-07-18
Materials Chemistry and Physics
Abstract:This work studies the hot corrosion behavior of GH4169 Ni-based superalloy, deposited with a mixture of salts comprising 95wt.% Na 2 SO 4 and 5wt.% NaCl, across three distinct temperatures (i.e., 650 °C, 800 °C and 950 °C). Corrosion and non-corrosive exposure experiments were compared, yielding data on mass loss and gain, respectively. Material characterization results revealed that the corrosion layer was mainly comprised of Cr 2 O 3 , Fe 2 O 3 , NiO, Al 2 O 3 , TiO 2 , NbS 2 and MoS 2 . Notably, as the temperature ascended from 650°C to over 800°C, the corrosion mechanisms underwent a transition from pitting to uniform corrosion, corresponding to low-temperature hot corrosion and high-temperature hot corrosion, respectively. At 650°C, a large number of semi-ellipsoidal corrosion pits manifested on the surface. Conversely, at 800°C and 950°C, the corrosion layer on the surface exhibited nearly uniform spallation. The pit growth model and spallation dynamics model were, respectively, developed based on the observed microstructure features. The models serve as tools for quantitative examination of the hot corrosion process of the superalloy at different temperatures.
materials science, multidisciplinary