Effect of pre-oxidation on the moderate-temperature hot corrosion behavior of CoNiCrAlY-YSZ thermal barrier coatings
Zhiqiang Yang,Chaoyong Luo,Xiaojun Zan,Jun Zhang,Weidong Liu,Wei Wang
DOI: https://doi.org/10.1016/j.surfcoat.2023.129947
IF: 4.865
2023-09-03
Surface and Coatings Technology
Abstract:The hot corrosion behavior of the normal and pre-oxidation thermal barrier coatings in two corrosive media (Na 2 SO 4 + NaVO 3 and Na 2 SO 4 + NaVO 3 + NaCl) was conducted in this article. Before the hot corrosion experiment, the optimal pre-oxidation conditions were selected to form a continuous single thin layer of α-Al 2 O 3 on the coating surface. The results showed that the coatings exhibit different failure behaviors in two corrosive media, and the mechanism of hot corrosion was explained. Notably, a coupling effect was observed among Na 2 SO 4 , NaVO 3 , and NaCl. Na 2 SO 4 drove the basic corrosion attack on the ceramic top coat, thermally grown oxide (TGO), and the bond coat. Meanwhile, NaVO 3 primarily strengthened the attack of Na 2 SO 4 on the ceramic top coat, while NaCl enhanced the attack of Na 2 SO 4 on TGO and bond coat. Furthermore, the pre-oxidation treatment effectively reduced the oxidation of the bond coat and the thickness of BDZ, and better extended the life of TBCs.
physics, applied,materials science, coatings & films