Abstract:The oxide scales on a Ti-2Al-2.5Zr alloy with and without pre-oxidation oxidised at 300 degreesC in an alkaline steam for approximately 13 000 h were studied by SEM, XRD, XPS and in situ AES techniques. Some of the samples were subjected to 400 degreesC deionised water steam at a pressure of 10 MPa for 72 h for pre-oxidation, The result showed that the oxide scales on the Ti-2Al-2.5Zr alloy were composed of Al2TiO5 (TiO2Al2O3,), TiO2, Ti3O5, Ti2O3, Al2O3 and TiO. A comparison study has been carried out between the pre-oxidised and without pre-oxidised Ti-2Al-2.5Zr to determine the influence of pre-oxidation upon the properties of oxidation resistance. The oxidation kinetics showed that the weight gains of the pre-oxidised samples were much less than that of the controlled samples, which was consistent with the results by in situ AES analysis. The AES results showed that the whole thickness of the pre-oxidised sample (approx. 33 000 Angstrom) was thinner than that of the controlled one (approx. 40000 Angstrom). in contrast the pattern for the stable oxide scale was reversed, i.e. the pre-oxidised sample was much thicker. Thus pre-oxidation is an effective method to improve the oxidation resistance of Ti-2Al-2.5Zr. (C) 2001 Elsevier Science B.V. All rights reserved.

The Effect of Pre-Oxidation on the Oxidation Behaviour of Ti-alloy at 300°C in an Alkaline Steam

Effect of Pre-Oxidation on the Oxidation Behavior of Ti-2Al-2.5Zr Alloy at 300°C in an Alkaline Steam

Characterisation of the oxide scale on a Ti–2Al–2.5Zr alloy with and without pre-oxidation in an alkaline steam at 300°C

Characterisation of the oxide scale on a Ti-2Al-2.5Zr alloy with and without pre-oxidation in an alkaline steam at 300 degrees C

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

Effect of Pre-Oxidation on the Steam Oxidation of Heat-Resistant Steel T92

Effect of Al content on 1200 °C steam oxidation behavior of Cr-based coatings on TZM alloy

Improving the Cyclic‐Oxidation Resistance of Ti3AlC2at 550°C and 650°C by Preoxidation at 1100°C

Effect of Pre-Oxidation on High-Temperature Oxidation Behavior of Al-Si Coating on Nickel-Based Superalloy

Characterization of Oxide Layers on Ti–2Al–2.5Zr and Ti–4Al–2V Alloys Oxidized at 300 °C in a Neutral Water Steam

Improvement of Intermediate-Temperature Oxidation Resistance of Ti3AlC2 by Pre-Oxidation at High Temperatures

Effect of Pre-Oxidation on the Hot Corrosion of CoNiCrAlYRe Alloy

Early oxidation behavior of Ti50Al and Ti45Al8Nb alloys

TEM Observation of Oxide Scale Formed on a Ti–Al–Zr Alloy Oxidized at 360°C in Alkaline Steam

Influence of Low-Temperature Pre-oxidation by Ozone on Corrosion Resistance of T91 Steel in Steam at 600 °C

Improving hot corrosion resistance of aluminized TiAl alloy by anodization and pre-oxidation

High Temperature In-situ X-ray Diffraction Study of the Oxidation of the Ti3Al Based Alloys

Effects of Pack Cementation Aluminizing and Vapor Aluminizing on Oxidation Behavior of P92 Steel in Saturated Steam at 650 C

Oxidation Behavior of Cr1-xAlx Coated Zr-4 Alloy under 1200 °C High Temperature Steam Environment

Effect Of Thermal Oxidation Duration On Microstructure And Properties Of Ti6al4v Alloy