Oxidation behavior of 316L austenitic stainless steel in high temperature air with long-term exposure
Xi Huang,Kai Xiao,Xiaodong Fang,Zicheng Xiong,Lihua Wei,Pengcheng Zhu,Xiaoyan Li
DOI: https://doi.org/10.1088/2053-1591/ab96fa
IF: 2.025
2020-06-01
Materials Research Express
Abstract:Abstract The oxidation behavior of 316L stainless steel exposed at 400, 600 and 800 °C air for 100, 500 and 1000 h was investigated using different characterization techniques. Weight gain obeys a parabolic law, but the degree of deviation of n index is increasingly larger with the increase of temperature. A double oxide film, including Cr 2 O 3 and Fe 2 O 3 oxide particles in outer and FeCr 2 O 4 oxides in inner, is observed at 400 °C. As regards to samples at 600 °C, a critical exposure period around 100 h exists in the oxidation process, at which a compact oxide film decorated with oxide particles transforms to a loose oxide layer with a pore-structure. In addition, an oxide film containing Fe-rich outer oxide layer and Cr-rich inner oxide layer is observed at 600 °C for 500 and 1000 h. Spallation of oxide scale is observed for all samples at 800 °C regardless of exposure periods, resulting in different oxidation morphologies, and the degree of spallation behavior is getting worse. A double oxide film with the same chemical composition as 600 °C is observed, and the thickness increases over exposure periods.
materials science, multidisciplinary