Effect of Boron on Stress Corrosion Resistance of S31254 Super‐Austenitic Stainless Steel After Cold Deformation
Taike Xiao,Xiaohong Liang,Zhuangzhuang Cao,Peide Han,Jinyao Ma,Hongli Liang,Caili Zhang,Nan Dong
DOI: https://doi.org/10.1002/srin.202400290
IF: 2.1258
2024-07-18
steel research international
Abstract:In this study, it is revealed that 5% cold deformation leads to the stabilization of the passive film and enhanced corrosion resistance of S31254, whereas a 30% deformation causes a reduction in corrosion resistance. The incorporation of boron enhances the uniformity of the deformation process, resulting in samples with improved resistance to pitting and intergranular corrosion. The effect of boron (B) on stress corrosion resistance of S31254 in the presence of residual stresses has been studied. The microstructure and corrosion resistance of S31254 containing B at different levels of cold deformation are analyzed in this study. In the results, it is shown that B favors the improvement of deformation uniformity of S31254. The grain boundary (GB) and slip bands have better corrosion resistance at 5% deformation, and the overall corrosion resistance is better than that of the undeformed state, with smaller passivation current density and narrower width of GB corrosion grooves, especially for the 40B samples. At 30% deformation, the overall corrosion resistance of 40B S31254 is better than 0B due to improved deformation uniformity.
metallurgy & metallurgical engineering