Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Huanchun Wu,Xiangbing Liu,Chaoliang Xu,Yuanfei Li,Jian Yin,Xiao Jin,Wenqing Jia,Wangjie Qian,Peng Wang,Yanwei Zhang

DOI: https://doi.org/10.3390/met14050489

IF: 2.695

2024-04-24

Metals

Abstract:The fatigue crack growth behavior of 304L austenitic stainless steel (SS) in a 325 °C high-temperature and high-pressure water environment were investigated by a corrosion fatigue test system, by electron back scatter diffraction (EBSD), and by a transmission electron microscope (TEM). The experimental results indicated that the crack growth rate (CGR) of 304L SS increases with increasing the stress intensity factor, stress level, and fatigue frequency (f). Compared to dissolved hydrogen (DH) in a high-temperature water environment, dissolved oxygen (DO) significantly enhances the CGR by about an order of magnitude higher. The crack tip of 304L SS after the corrosion fatigue test under higher stress levels is sharper, with more secondary cracks on the fracture surface, while the crack tip under lower stress levels is blunter with relatively fewer secondary cracks. The oxidation behavior at the crack tip was analyzed under different loading and water chemistry conditions, and a related effect on the crack tip and CGR was clarified.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the issue of corrosion fatigue behavior of 304L austenitic stainless steel in a high-temperature water environment at 325°C. Specifically, the researchers investigated the effects of different stress intensity factors, stress levels, fatigue frequencies, and water chemistry conditions (such as dissolved oxygen and dissolved hydrogen) on the crack growth rate (CGR) of 304L stainless steel through experiments. The main objectives include:

1. **Factors Affecting Crack Growth Rate (CGR)**:
- Investigate the effects of stress intensity factor (K), stress level (f), and fatigue frequency (f) on the crack growth rate of 304L stainless steel.
- Explore the impact of dissolved oxygen (DO) and dissolved hydrogen (DH) on the crack growth rate in a high-temperature water environment.

2. **Oxidation Behavior at the Crack Tip**:
- Analyze the oxidation behavior at the crack tip under different loading conditions and water chemistry conditions and its effect on the crack growth rate.
- Reveal the initiation mechanism of cracks in a high-temperature water environment.

3. **Crack Growth Path and Morphology**:
- Observe and analyze the crack growth path and morphology in a high-temperature water environment, especially the microstructural characteristics at the crack tip.

Through these studies, the paper aims to provide scientific evidence for the corrosion fatigue performance of 304L stainless steel in the high-temperature and high-pressure water environment of nuclear power plants, thereby providing guidance for material selection and design.