Abstract:Dry storage canisters of used nuclear fuels are fabricated using SUS 304L stainless steel. Chloride-induced stress corrosion cracking (CISCC) is one of the major failure modes of dry storage canisters. The cracked canisters can be repaired by friction stir welding (FSW), a low-heat input 'solid-phase' welding process. It is important to evaluate the ClSCC resistance of the friction stir welded material. Stress corrosion cracking (SCC) studies were carried out on mill-annealed base materials and friction stir welded 304L stainless U-bend specimens in 3.5% NaCl + 5 N H2SO4 solution at room temperature and boiling MgCl2 solution at 155 °C. The engineering stress on the outer fiber of the FSW U-bend specimen was ~60% higher than that of the base metal (BM). In spite of the higher stress level of the FSW, both materials (FSW and BM) showed almost similar SCC failure times in the two different test solutions. The SCC occurred in the thermo-mechanically affected zone (TMAZ) of the FSW specimens in the 3.5% NaCl + 5 N H2SO4 solution at room temperature, while the stirred zone (SZ) was relatively crack-free. The failure occurred at the stirred zone when tested in the boiling MgCl2 solution. Hydrogen reduction was the cathodic reaction in the boiling MgCl2 solution, which promoted hydrogen-assisted cracking of the heavily deformed stirred zone. The emergence of the slip step followed by passive film rupture and dissolution of the slip step could be the SCC events in the 3.5% NaCl + 5 N H2SO4 solution at room temperature. However, the slip step height was not sufficient to cause passivity breakdown in the fine-grained SZ. Therefore, the SCC occurred in the partially recrystallized softer TMAZ. Overall, the friction-stirred 304L showed higher tolerance to ClSCC than the 304L base metal.

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Anomalous Evolution of Corrosion Behaviour of Warm-Rolled Type 304 Austenitic Stainless Steel

On the corrosion cracking of austenitic stainless steel in molten solar salt: Experiments and modeling

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Environmentally-assisted cracking of electropolished 316L stainless steel in molten FLiNaK salt

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Insights from electrochemical crack tip modeling of atmospheric stress corrosion cracking

Observations of Stress Corrosion Cracking in Pipeline Steel in Corrosive Seawater Environment Including Detailed Observation of the Crack Initiation Mechanism

Stress Corrosion Cracking of Duplex Statinless Steel in High Temperature Water.

Experimental Investigation of Stress Corrosion Characteristics for 16mnr Steel in Nitrate Solution

Experimental study on mechanical properties and low-cycle fatigue behaviour of stainless steels subjected to salt spray and dry/wet cycle

Chloride-Induced Stress Corrosion Cracking of Friction Stir-Welded 304L Stainless Steel: Effect of Microstructure and Temperature

Study on stress corrosion behavior of 316L austenitic stainless steel in hot NaOH solution

Elevated temperature molten salt corrosion study of SS304L austenitic boiler steel

Impact of temperature on corrosion behavior of austenitic stainless steels in solar salt for CSP application: An electrochemical study

Investigation of stress corrosion cracking behavior and mechanism analysis of a 1900 MPa-grade ultra-high-strength stainless steel

Discussion on Factors of Unstable 304 Stainless Steel Stress Corrosion Cracking

Corrosion behavior of metastable AISI 321 austenitic stainless steel: Investigating the effect of grain size and prior plastic deformation on its degradation pattern in saline media

Corrosion behaviors and protective layer stabilization mechanism of 316 stainless steel in NaCl–KCl–NaF reciprocal salts at high temperatures

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads