Abstract:Environmentally-assisted cracking is a well-known and extensively studied phenomenon in light water reactor environments but remains relatively unexplored in proposed molten salt reactor systems where the mechanisms at play are expected to be quite different. Here, slow strain rate testing has been performed on 316L stainless steel tensile specimens during simultaneous exposure to a molten LiF-KF-NaF eutectic salt environment at 600 °C with a strain rate between 1E-5 to 1E-7 s -1 . Sample ductility and ultimate tensile strength were both observed to decrease for slower strain rates/longer salt exposures. Post-mortem characterization of fractured specimens revealed Fe deposits and Cr- and O-rich precipitates decorating surface grain boundaries and crack surfaces, suggesting a cracking mechanism driven by embrittlement of the crack tip due to oxide formation. Unlike previous studies, intergranular Cr corrosion into the bulk was not observed, and distinct differences in surface morphology between electropolished and non-electropolished sample surfaces are reported. Trace metal salt chemistry measurements showed accumulation of 316L alloying elements over the course of the tests. It appears likely that the surface oxide layer induced by electropolishing, in addition to oxygen and moisture impurities in the salt, led to the formation of LiCrO 2 which had a net passivating effect that prevented significant bulk corrosion, though some interplay between mechanical and environmental stressors is still observed.

On the corrosion cracking of austenitic stainless steel in molten solar salt: Experiments and modeling

Corrosion and electrochemical investigations for stainless steels in molten Solar Salt: The influence of chloride impurity

A Corrosion Cracking Mechanism-Based Model with Molten Salt Corrosion Damage Coupling the Effect of Chloride Impurity and Plastic Deformation

Impact of temperature on corrosion behavior of austenitic stainless steels in solar salt for CSP application: An electrochemical study

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Corrosion behaviors and protective layer stabilization mechanism of 316 stainless steel in NaCl–KCl–NaF reciprocal salts at high temperatures

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Corrosion behavior and mechanism of 316 stainless steel in NaCl–KCl–FeCl3 molten salt and vapor at 300°C

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

Environmentally-assisted cracking of electropolished 316L stainless steel in molten FLiNaK salt

High temperature corrosion behaviour of the 316 stainless steel in NaCl-KCl-AlCl 3 molten salt and its vapour

Impacts of Applied Stresses on High Temperature Corrosion Behavior of HR3C in Molten Salt

Corrosion behavior and mechanism of 316 stainless steel in NaCl-KCl-ZnCl2 molten salts at high temperature

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Corrosion behavior of carburized 316 stainless steel in molten chloride salts

Corrosion Behavior of 20G and TP347H in Molten LiCl-NaCl-KCl Salt

Experimental study on mechanical properties and low-cycle fatigue behaviour of stainless steels subjected to salt spray and dry/wet cycle

High-temperature Dynamic Corrosion Mechanisms of Austenitic Stainless and Carbon Steels in Nitrates for Concentrating Solar Power

Effect of Molten Salts Composition on the Corrosion Behavior of Additively Manufactured 316L Stainless Steel for Concentrating Solar Power

Effect of Temperature and Impurity Content to Control Corrosion of 316 Stainless Steel in Molten KCl-MgCl2 Salt

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment