Abstract:Reinforced concrete structures exposed to marine environments often experience chloride ingress, reinforcement corrosion, and corrosion‐induced cracking. The electrochemical repair method is a promising concrete rehabilitation technique with advantages of non‐destructive and economic performance in crack repair, chloride removal, and corrosion protection, which is particularly suitable for structures exposed to marine environments. This work presents an innovative methodology for modeling the mechanical, transport, and chemical process during electrochemical treatment for marine concrete structures. The entire process from concrete cracking up to repairing can be successfully reproduced and digitally visualized. The first sub‐model calculates the corrosion‐induced cracking process at the mesoscopic level with the consideration of local mechanical variances of concrete composites. Then, a reactive transport sub‐model is established to reveal the interactions and electrochemical reactions among various species of ions. A crack repair sub‐model is built to visualize the moving interface between chemical deposition and crack surface. Through combining the three sub‐models, the interconnected influencing factors in practical engineering can be quantitively investigated. The calculation results show that, compared with electrolyte concentration, the influence of current density on crack closure rates are more obvious. Other factors such as steel reinforcement diameter and crack distribution pattern, which have not been previously reported are highlighted. These findings can guide the application of electrochemical repair in practical engineering.

A Corrosion Cracking Mechanism-Based Model with Molten Salt Corrosion Damage Coupling the Effect of Chloride Impurity and Plastic Deformation

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

Study of mechano-electrochemical model: a numerical and experimental approach

A coupled mechano-chemical peridynamic model for pit-to-crack transition in stress-corrosion cracking

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Corrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste

On the corrosion cracking of austenitic stainless steel in molten solar salt: Experiments and modeling

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Chemical Corrosion-Water-Confining Pressure Coupling Damage Constitutive Model of Rock Based on the SMP Strength Criterion

Corrosion-induced concrete cracking model considering corrosion product-filled paste at the concrete/steel interface

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Mechanical–transport–chemical modeling of electrochemical repair methods for corrosion‐induced cracking in marine concrete

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Modelling damage evolution of carbon fiber-reinforced epoxy polymer composites in seawater sea sand concrete environment

A Damage-Effect-involved Phenomenological Crystal Plasticity Model and Computational Methods for Mechanical Responses of FeCrAl Alloys

Experiments and cellular automata simulation of corrosion and protection of Hastelloy X in high-temperature chloride molten salts

Salt Cavern Thermal Damage Evolution Investigation Based on a Hybrid Continuum-Discrete Coupled Modeling

An improved crack growth model of corrosion fatigue for steel in artificial seawater

Modeling of the corrosion-induced crack in concrete contained transverse crack subject to chloride ion penetration