Stress Corrosion Cracking of Duplex Statinless Steel in High Temperature Water.

T. Kuroda,K. Bunno,F. Matsuda

DOI: https://doi.org/10.2207/QJJWS.13.116

Abstract:Relation between microstructure and stress corrosion cracking in high temperature water for duplex stainless steel was investigated using transmission electron microscopy and fractography.The samples were solution-treated at various temperatures and then sensitized at 923 K for 72 ks. The slow strain rate testing (SSRT) was carried out at 562 K in water with 8 ppm dissolved oxygen under 8 MPa pressure at a strain rate of 4.17×10-6 s-1.The volume fraction of α phase and Cr2N in the α phase increasedd with increasing the solution treatment temperature.For the sensitized sample, M23C6 precipitated at α/γ interface, the bowing area of secondary austenite, namely γ* phase occurred, and σ phase precipitated at the γ*/α interface. They increased with decreasing solution treatment temperature and with decreasing the volume fraction of α phase.The stress corrosion cracking in high temperature water hardly occurred for the solution-treated samples. The reduction of area of the sensitized sample was much lower than that of the solutiontreated samples and decreased with decreasing solution treatment temperature, because the γ* phases near the M23C6 and the σ phase were predominantly corroded and resolved during the test.

Materials Science,Engineering