Abstract:Stress corrosion cracking (SCC) is one of the main ageing mechanism in light water reactor (LWR). 316L austenitic stainless steel was adopted in nuclear industry for its relatively high corrosion resistance. The SCC of austenitic stainless steel may occur as it is subjected to both the tensile stress and the caustic medium, with regard to maintaining the structural integrity of components in nuclear power plant, an accurate prediction and efficient assessment of the component lifetime is significant and necessary. The stress corrosion crack propagation behavior of the 316L stainless steel elbow of nuclear power plant was investigated through a numerical simulation method. Firstly a finite element (FE) model was created for the stainless steel thick-walled elbow (the outer diameter is 355.6 mm, the inner diameter is 275.6 mm), with a semi-elliptical shaped 3D defect introduced at the internal surface of the elbow as the geometry of the crack, which was consistent with a practical crack, the crack opening displacement (delta(i)) was determined by the calculations through the Dugdale model; subsequently, according to the FE calculation results, establish the fitting formula of the stress intensity factor (K) varying with the crack depth (a) and additional stress (P), and the fitting formula of the stress corrosion crack propagation rate (da/dt) for elbows under two types of cold work deformation was deduced through the combination with the experimental data, the crack propagation time was then calculated using a iterative method for cracks which evolved from different initial crack depth values to certain crack depth values. The calculation results provided effective reference criterion for the nuclear power plant safety assesment. This investigation demonstrated that, when the cold deformation extent of the elbow part is relatively small (with the hardness of 230 similar to 245 HV) and it is under the ideal condition (no initial additional stress), it takes around 57 a for the stress corrosion crack to penetrate the elbow, when the initial additional stress was elevated to 200 MPa, the elbow failure time was shrinked to 1/5 (no stress release), 2/7 (half-stress release) and 3/7 (total stress release) of the former; keep the same initial additional stress (200 MPa) and increase the cold work deformation extent (the hardness was increased from 230 similar to 245 HV to 275 similar to 300 HV), the elbow failure time was shortened to 2/5 (no stress release), 3/8 (half-stress release) and 1/3 (total stress release) for the elbow part with higher cold deformation extent compared to the part with lower cold deformation extent, thus it was observed that both the decrease of the extent of stress relaxation and the increase of the extent of cold work deformation contributed to the reduction of the residual life of the nuclear power plant 316L stainless steel elbow.

Stress Corrosion of Austenitic Stainless Steel 316L in High Temperature Water

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Effects of Chloride and Oxygen on Stress Corrosion Cracking of Cold Worked 316/316L Austenitic Stainless Steel in High Temperature Water

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Evaluation of Stress Corrosion Cracking Susceptibility of Forged 316 Stainless Steel in Simulated Primary Water

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

A Research on the Corrosion and Stress Corrosion Cracking Susceptibility of 316L Stainless Steel Exposed to Supercritical Water

Corrosion Fatigue Behavior and Crack-Tip Characteristic of 316LN Stainless Steel in High-Temperature Pressurized Water

Stress Corrosion Cracking Behavior of Cold-Drawn 316 Austenitic Stainless Steels in Simulated Pwr Environment

Life Prediction for Stress Corrosion Behavior of 316l Stainless Steel Elbow of Nuclear Power Plant

Stress Corrosion Cracking of 316l Haz for 316l Stainless Steel/Inconel 52m Dissimilar Metal Weld Joint in Simulated Primary Water

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Stress Corrosion Crack Growth Behavior of Type 310S Stainless Steel in Supercritical Water

Stress Corrosion Cracking of Uni-Directionally Cold Worked 316ng Stainless Steel in Simulated Pwr Primary Water with Various Dissolved Hydrogen Concentrations

Stress Corrosion Cracking in the Heat Affected Zone of A Stainless Steel 308L-316L Weld Joint in Primary Water

A Study on the Propagation of Chloride-Induced Stress Corrosion Cracking for Austenitic Stainless Steel at Corrosion Environment

Effect of Temperature and Dissolved Oxygen on Stress Corrosion Cracking Behavior of P92 Ferritic-Martensitic Steel in Supercritical Water Environment

Insights into the Stress Corrosion Cracking Propagation Behavior of Alloy 690 and 316 L Stainless Steel in KOH Versus LiOH Oxygenated Water

Stress Corrosion Crack Growth Behavior of Domestic Alloy 52 Dissimilar Weld Metal in High Temperaturre Water

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Corrosion Fatigue Behavior of 316LN Stainless Steel Hollow Specimen in High-Temperature Pressurized Water