Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Effect of different loading conditions on corrosion fatigue crack growth rate of a nickel-based alloy in supercritical water

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Stress corrosion cracking susceptibility of a new nickel‐based alloy in different environments

The Effects of Inhomogeneous Microstructure and Loading Waveform on Creep-Fatigue Behaviour in a Forged and Precipitation Hardened Nickel-Based Superalloy

Effect of Cold Work on the Stress Corrosion Cracking Behavior of Alloy 690 in Supercritical Water Environment

The Effect of Nano-Sized Precipitates on Stress Corrosion Cracking Propagation of Alloy 718 under Constant Loads in PWR Primary Water

Effect of temperature and medium environment on corrosion fatigue behavior of Inconel 625

Characterizing the Effect of Creep on Stress Corrosion Cracking of Cold Worked Alloy 690 in Supercritical Water Environment

Effect of Intergranular Carbides on the Cracking Behavior of Cold Worked Alloy 690 in Subcritical and Supercritical Water

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Stress Corrosion Crack Growth Behavior of Type 310S Stainless Steel in Supercritical Water

Strain Rate Dependence of the Effect of Intergranular Carbides on the Resistance to Stress Corrosion Cracking Initiation of Alloy 690 in Simulated Pwr Primary Water

Corrosion fatigue testing: the combined effect of stress and high temperature corrosion

High-temperature hot-corrosion effects on the creep–fatigue behavior of a directionally solidified nickel-based superalloy: Mechanism and lifetime prediction

The mechanism of thermal corrosion fatigue (TCF) on nickel-based single crystal superalloy and the corresponding structure shape effect

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

Stress Corrosion of Austenitic Stainless Steel 316L in High Temperature Water

Insights into the Superior Stress Corrosion Cracking Resistance of FeCrAl Alloy in High Temperature Hydrogenated Water: the Critical Role of Grain Boundary Oxidation

Effect of Stress Ratio on the Fatigue Crack Propagation Behavior of the Nickel-based GH4169 Alloy

Corrosion Characteristics and Mechanisms of Typical Ni-based Corrosion-Resistant Alloys in Sub- and Supercritical Water

Corrosion and Stress Corrosion Cracking Susceptibility of Type 347H Stainless Steel in Supercritical Water