Abstract:This work describes a viable hydrogen-induced sensitisation process toward stress corrosion cracking in chromia-forming nickel base alloys owing to oxidation by water. A mechanistic chemical understanding of the stress corrosion based on repeated cracking and re-healing of the oxide scale emerges from experiment-guided first-principles calculations. Piggybacking processes during repeated oxide scale cracking-healing cycles are understood to cause sensitisation towards the formation and growth of macroscopic cracks. Under light-water reactor conditions, the healed oxide scale comprises an outer region composed of chromium depleted nickel ferrite, and non-protective chromia, nickel oxide, nickel hydroxide. An inner nickel iron chromite layer provides the passivating barrier that controls the oxidation rate at a steady state. Early during the re-healing of a crack in the oxide scale, water is conveyed to the alloy/scale interface by hydration/dehydration of composite nickel oxy-hydroxide Ni(OH) 2 ∙NiO inclusions in the scale. At later stages, Ni(OH) 2 ∙NiO serves as oxidant of preferentially chromium, while hydrogen is released as H 2 (g) into the primary water or becomes picked up by the alloy, possibly while assisting in the reduction of NiO to form nickel metal particles. Oxidation by water equivalents at the confining alloy/scale interface favours hydrogen pick-up in the alloy that becomes increasingly detrimental owing to enrichment and inward diffusion of hydrogen along alloy grain boundaries where pinning of alloy vacancies causes mitigation of outward diffusion of chromium, which in turn hampers crack re-healing while promoting alloy embrittlement.

Effect of dissolved oxygen and hydrogen on the stress corrosion cracking behavior of alloy 600 in high temperature water

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Impact of Diffusible Hydrogen on Corrosion of Alloy 600 at 288°C: an In-Situ Electrochemical Study

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Quantitatively evaluating the contribution of intergranular carbides, Cr-depleted zone, and grain boundary to intergranular stress corrosion cracking of Alloy 600 in a simulated boiling water reactors environment with high oxygen concentrations

Effects of alternating dissolved oxygen and dissolved hydrogen on the corrosion behavior of alloy 52 in high temperature high pressure water

Effects of the Cr-Depletion on the Stress State of the Sublayer of Ni-Base Alloys Oxidized in High Temperature Water

Stress corrosion crack initiation in Alloy 690 in high temperature water

Stress-Corrosion Cracking Sensitization by Hydrogen upon Oxidation of Nickel-base Alloys by Water – an Experiment-Guided First-Principles Study

Stress corrosion behavior and mechanism of Ti6321 alloy in seawater with different dissolved oxygen concentrations

Diffusible Hydrogen Facilitated Stress Corrosion Cracking in 316 Stainless Steel Using In-Situ Gaseous Hydrogen Charging in Simulated PWR Environment

The role of hydrogen in promoting differences in fatigue crack growth rates observed in Type 304/304L stainless steel at elevated temperature

Corrosion behavior of NiCrFe Alloy 600 in high temperature, hydrogenated water

A cracking oxygen story: A new view of stress corrosion cracking in titanium alloys

CORROSION BEHAVIOR OF SUPER-AUSTENITIC STAINLESS STEEL AL-6XN IN SUPERCRITICAL WATER

Effect of different loading conditions on corrosion fatigue crack growth rate of a nickel-based alloy in supercritical water

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Microstructural understanding of the oxidation and inter-diffusion behavior of Cr-coated Alloy 800H in supercritical water

Combined effect of hydrogen embrittlement and corrosion on the cracking behaviour of C110 low alloy steel in O2-contaminated H2S environment

Investigations on the SCC initiation behavior of cold worked 316L in high temperature oxygenated water at constant loads

Effect of oxygen concentrations on the corrosion behavior of a duplex-phase FeNiCrCuAl high entropy alloy in supercritical water