Effect of high temperature on the corrosion behavior and passive film composition of 316 L stainless steel in high H2S-containing environments

Zhu Wang,Zhe Feng,Lei Zhang
DOI: https://doi.org/10.1016/j.corsci.2020.108844
IF: 7.72
2020-09-01
Corrosion Science
Abstract:<p>The effect of high temperature on the corrosion behaviour and passive film composition of 316 L stainless steel in high H<sub>2</sub>S-containing environments was investigated. The results showed that high temperature promoted the formation of thicker but more defective passive film. The dominant composition of passive films converted from Fe, Cr to Ni, Fe as the temperature increased from 30 °C to 130 °C, due to the decreased stability of Cr at high temperature. Besides, high temperature led to the higher content of sulfides in the passive film, attributed to the enhanced adsorption of S species.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper mainly explores the effects of high temperature on the corrosion behavior and passivation film composition of 316L stainless steel in a high hydrogen sulfide (H₂S) environment. Specifically, the study found: 1. **High temperature leads to increased corrosion**: As the temperature rises from 30°C to 130°C, the corrosion resistance of 316L stainless steel significantly decreases. High temperature promotes the formation of the passivation film, but the formed passivation film is thicker and has more defects, leading to a decline in protective performance. 2. **Changes in passivation film composition**: The main components of the passivation film shift from iron (Fe) and chromium (Cr) to nickel (Ni) and iron (Fe). This is mainly because the stability of chromium (Cr) significantly decreases at high temperatures. 3. **Increase in sulfides**: High temperature promotes the formation of sulfides in the passivation film, which is due to the enhanced adsorption of sulfur (S) species. 4. **Reduction in chromium content**: High temperature leads to a decrease in the chromium content in the passivation film, while the sulfur content increases, causing the degradation of the passivation film. In summary, this study aims to reveal the corrosion mechanism of 316L stainless steel in a high hydrogen sulfide environment under high temperature conditions and the changes in its passivation film, providing theoretical basis and technical support for the application of related materials.