Influence of Oxygen Content on the Corrosion Behaviour of 316 L Stainless Steel in the Simulated Cathodic Environment of Proton Exchange Membrane Fuel Cell

D. G. Li,D. R. Chen,P. Liang

DOI: https://doi.org/10.1016/j.jallcom.2021.159695

IF: 6.2

2021-01-01

Journal of Alloys and Compounds

Abstract:316 L stainless steel (316 L SS) was melted in three different vacuum degree environments, and the oxygen content of the melted 316 L SS was measured using a routine method (ISO 15351:1999). The results revealed that oxygen content decreased with increasing vacuum degree during the melting process. Then, the influence of oxygen content on the corrosion behaviour of 316 L SS in the simulated cathodic environment of proton exchange membrane fuel cells (PEMFCs) was investigated using potentiodynamic curves, electrochemical impedance spectroscopy (EIS), Mott-Schottky plots, auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS). The results show that decreasing the oxygen content can significantly increase the passivity of 316 L SS in the simulated cathodic environment. EIS and Mott-Schottky plot results show that a passive film can be formed on 316 L SS in a simulated cathodic environment, and the compactness and resistance of the passive film increase with decreasing oxygen content, indicating improved corrosion protection of the passive film. Meanwhile, the passive film exhibits semiconductive characteristics, and the defect density decreases with decreasing oxygen content, implying increased homogeneity and stability of the passive film on 316 L SS. The AES and XPS results show that the passive film on 316 L SS consists of an inner Cr2O3 film and an outer iron oxide film, in which the thickness of the passive film and the content of the inner Cr2O3 film increase with decreasing oxygen content. Thus, it can be concluded that the corrosion protection of the passive film on 316 L SS increases with decreasing oxygen content considering the main corrosion protection contribution of the Cr2O3 film. (C) 2021 Published by Elsevier B.V.