Influence of Heat Treatment on Corrosion Behaviors of 316L Stainless Steel in Simulated Cathodic Environment of Proton Exchange Membrane Fuel Cell (PEMFC)

D. G. Li,D. R. Chen,P. Liang

DOI: https://doi.org/10.1016/j.ijhydene.2020.08.041

IF: 7.2

2020-01-01

International Journal of Hydrogen Energy

Abstract:The influences of two types of heat-treatments on the corrosion behavior of 316L SS in the simulated cathodic environment of PEMFC, are investigated using potentiodynamic curve, electrochemical impedance spectroscopy (EIS), Mott-Schottky plot and auger electron spectroscopy (AES), respectively. The results show that 316L SS is in the passive state within the potential region from -0.1V(SCE) to 0.8V(SCE) in the simulated cathodic environment of PEMFC, and a passive film can be formed on 316L SS. The passivity of 316L SS in the simulated cathodic environment of PEMFC firstly increases and then degrades with the increased solid solution temperature or time, and the best passivity corresponds to the solid solution temperature at 1050 degrees C for 40 min among other solid solution treatments. While 316L SS heat-treated with the solid solution treatment at 1050 degrees C for 40 min plus aging treatment at 900 degrees C for 4 h, also has the best passivity in the same solution among other solid solution plus aging treatments. The best corrosion protection, lowest donor density and the highest thickness of the passive film corresponding to the solid solution temperature at 1050 degrees C for 40 min among other solid solution or solid solution plus aging heat treatments, and this treatment is mostly suitable for improving the anti-corrosion property of 316L SS in the simulated cathodic environment of proton exchange membrane fuel cell (PEMFC). (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.