Improvement of corrosion resistance and electrical conductivity of a Cr–C coated heat-assisted forming stainless steel bipolar plate for proton exchange membrane fuel cell

Yu Leng,Daijun Yang,Junying Min,Xinyu Lv,Jian Yang,Junfeng Qian,Pingwen Ming,Cunman Zhang

DOI: https://doi.org/10.1016/j.ijhydene.2024.05.194

IF: 7.2

2024-05-19

International Journal of Hydrogen Energy

Abstract:Heat-assisted forming is gaining increasing attention for its potential in improving the formability and quality of metallic bipolar plate (BPP) of proton exchange membrane fuel cell (PEMFC). However, the effects of heat-assisted forming and the subsequent coating process on corrosion resistance and electrical conductivity of stainless steel BPP still remain unclear. This work proposes a way to improve simultaneously the corrosion resistance and electrical conductivity of heat-assisted forming stainless steel BPP by depositing a Cr–C coating directly on its surface without removing the oxide layer using the magnetron sputtering method. Potentiodynamic tests indicate that self-corrosion current density and corrosion current density at 1.0 V (vs. Ag/AgCl) of the Cr–C coated heat-assisted forming SS316L BPP prepared under 900 °C for 10 min are 0.021–0.040 μA cm −2 and 77.54 μA cm −2 , respectively, both of which are smaller than those of coated SS316L BPP formed under room temperature. In addition, the contact resistance is close to that of the gold-plated copper plate under the same pressure. The corrosion resistant intermediate oxide layer and conductive network formed between Cr–C coating and metal substrate through defects of oxide layer may be the main reason for improvement of its corrosion resistance and electrical conductivity, respectively.

energy & fuels,electrochemistry,chemistry, physical