Improving hot corrosion resistance of aluminized TiAl alloy by anodization and pre-oxidation
Yuan-tao HU,Lei ZHENG,Hao-jie YAN,Lian-kui WU,Xiang-jun LIN,Fa-he CAO,Mei-yan JIANG
DOI: https://doi.org/10.1016/s1003-6326(20)65487-5
IF: 3.752
2021-01-01
Transactions of Nonferrous Metals Society of China
Abstract:To shield TiAl alloy from hot corrosion attack, a compact protective coating was fabricated by the combination of aluminizing, anodization and pre-oxidation. The hot corrosion behavior of the coated-TiAl specimen was investigated in the mixture salt consisting of 75 wt.% Na<sub>2</sub>SO<sub>4</sub> and 25 wt.% NaCl at 700 °C. Results indicated that the anodization and pre-oxidation were beneficial to the generation of Al<sub>2</sub>O<sub>3</sub> layer, which could act as a diffusion barrier to prevent the molten salts and oxygen from diffusing into the alloy during exposure to a hot corrosion environment while the aluminizing coating could provide sufficient aluminum source to support the continuous formation of Al<sub>2</sub>O<sub>3</sub> layer. Moreover, the internal stress of the coating was reduced due to the formation of a gradient coating consisting of TiAl<sub>3</sub> and TiAl<sub>2</sub>.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?