Hot corrosion behavior of electrodeposited SiO2 coating on TiAl alloy

Lian-Kui Wu,Jing-Jia Wu,Wei-Yao Wu,Hao-Jie Yan,Mei-Yan Jiang,Fa-He Cao
DOI: https://doi.org/10.1016/j.corsci.2020.108827
IF: 7.72
2020-09-01
Corrosion Science
Abstract:<p>To improve the hot corrosion resistance, thickness controllable SiO<sub>2</sub> coating was electrodeposited on TiAl alloy. The hot corrosion behavior of the specimens contaminated with 75 wt.% Na<sub>2</sub>SO<sub>4</sub> + 25 wt.% NaCl salt mixture was investigated at 700 °C. Results showed that the generation of compact amorphous SiO<sub>2</sub> embedded with Na<sub>2</sub>Si<sub>4</sub>O<sub>9</sub> and cristobalite was responsible for the enhanced hot corrosion resistance. Moreover, the SiO<sub>2</sub> coating does not only act as a diffusion barrier to sulfur and chlorine but also decreases the oxygen partial pressure at the coating/alloy interface, therefore promoting the selective oxidation of Al to form protective Al<sub>2</sub>O<sub>3</sub> layer.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?