Abstract:PtAl and MCrAlY coating were prepared on the fourth generation single crystal superalloy. The isothermal oxidation tests of superalloys with different coatings were performed at 1150 °C and 1200 °C in a muffle furnace with static air for 500 h. The isothermal oxidation behavior and mechanism of two coatings at 1150 °C and 1200 °C was investigated. MCrAlY coating improved oxidation resistance by forming adhesive oxide scales with pegs, and PtAl coating formed dense and coherent oxide scales on surface to hinder the diffusion of oxygen. Compared with two coatings, a smaller oxidize increasing weight of PtAl coating (0.54 mg/cm 2 ) than MCrAlY coating (2.48 mg/cm 2 ) indicated that PtAl coating presented a better oxidation resistance during oxidation test at ultra high temperature, although a significant interdiffusion behavior occurred between PtAl coating and substrate. Besides, the interactive behavior between Ru and coatings was also investigated. Ru in fourth generation single crystal superalloy could diffuse into β-NiAl phase of coatings, maintaining the integrity of coatings. The major difference between MCrAlY coating and PtAl coating came in the amounts of β-NiAl phase, which leading to the difference on the oxidation resistance between MCrAlY and PtAl. The mechanism about influence of temperature on the oxidation property on bare alloy, MCrAlY-DD91 and PtAl-DD91 was also discussed. Ultra high temperature would promote more elements to participate in the reaction with oxygen, change the compositions of oxide scale and phases, resulting to the spallation of oxide scale and decrease of oxidation resistance.

Effect of Pt modification on hot corrosion resistance of NiCrAlYSi+AlY coating at 900 °C

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effect of Pt on Stress Rupture Properties of Pt-Modified Nickel Aluminide Coatings at 1100 °C

Influence of Pt on oxidation behavior of CoNiCrAlY alloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Hot corrosion of sputtered nanocrystalline coating with and without preoxidation and arc ion plating coating on a Ni-based single-crystal superalloy

Effect of Platinum and Pre-Oxidation on the Hot Corrosion Behavior of Aluminide Coating with NaCl at 1050 °C

Diffusion Characteristics and Structural Stability of Pt Modified Β-Nial/γ′-ni3al Within NiCoCrAl Alloy at High Temperature

Investigation on the tensile properties of PtAl and PtReAl coated Ni3Al-based single crystal superalloy

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

Hot Corrosion and Oxidation Behavior of Pt–Aluminide and Pt–Rh–Aluminide Coatings Applied on Nickle-Base and Cobalt-Base Substrates

Tensile crack inhibition of a PtReAl coated Ni 3 Al-based single crystal superalloy after long-term oxidation

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Effects of aluminised-coating on microstructure and properties of Ni–Co-base superalloys

Improved hot corrosion resistance of Al-gradient NiSiAlY coatings at 750 °C by pre-oxidation

Fatigue behavior of Pt-modified aluminum coated single crystal superalloy at 900 °C

Hot Corrosion and Electrochemical Behavior of NiCrAlY, NiCoCrAlY and NiCoCrAlYTa Coatings in Molten NaCl-Na2SO4 at 800 °C