Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Fatigue behavior of Pt-modified aluminum coated single crystal superalloy at 900 °C

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Pt-Al bond coat dependence on the high-cycle fatigue rupture and deformation mechanisms of a fourth-generation single crystal superalloy at various temperatures

High-temperature Oxidation Behavior of AlCoCrCuFeNi High-Entropy Alloy by Selective Laser Melting

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

Investigation on the tensile properties of PtAl and PtReAl coated Ni3Al-based single crystal superalloy

Effect of Pt on Stress Rupture Properties of Pt-Modified Nickel Aluminide Coatings at 1100 °C

Microstructural study of aluminide surface coatings on single crystal nickel base superalloy substrates

Tensile crack inhibition of a PtReAl coated Ni 3 Al-based single crystal superalloy after long-term oxidation

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Tuning the secondary reaction zone between PtAl coating and nickel based single crystal superalloy during high-temperature oxidation through regulating aluminizing time

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

Coating-assisted deterioration mechanism of creep resistance at a nickel-based single-crystal superalloy

Effect of Pt modification on hot corrosion resistance of NiCrAlYSi+AlY coating at 900 °C

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Microstructure evolution and interdiffusion behaviors of (Ni,Pt)Al coating with and without Re-diffusion barrier on IC21 substrate at 1100°C

Diffusion Characteristics and Structural Stability of Pt Modified Β-Nial/γ′-ni3al Within NiCoCrAl Alloy at High Temperature