Abstract:Pt-modified aluminide coating has attracted great attention due to its advantage of the integrated property in resisting both high temperature oxidation and hot corrosion. By the presence of Pt, the spallation trend of the grown oxide scale and the detrimental effect of S can be restrained at a very low level. Besides, Pt could promote alpha-Al2O3 formation and stabilize beta-NiAl phase. Thus Pt-modified aluminide (Pt-Al) coating has been widely used in some crucial applications requiring reliability and extended service life. There are mainly PtAl2, beta-(Ni, Pt) Al and gamma/gamma'-NiPtAl phases existing inside Pt-Al coating. In this work, a single phase PtAl2 coating was prepared on a Ni-based K38G superalloy through pulse-electroplating of Pt and pack aluminization under stepped heating mode. At 1100 degrees C, the isothermal oxidation behavior of the single phase PtAl2 coating was evaluated by thermogravimetric analysis (TGA). Cyclic oxidation test of the PtAl2 coating was performed within a vertical muffle furnace at the same temperature. The results indicate that the singular PtAl2 coating possesses quite good isothermal oxidation resistance. However, its resistance against cyclic oxidation is very poor. The cyclic stress induced by repeated heating and cooling has caused visible detachment of PtAl2 coating layer, and the spallation of PtAl2 in further would lead to a premature failure of the whole coating system. Partial spallation of PtAl2 layer, including undesirable consumption of Al inside beta-NiAl nearby the spallation acts the main reason responsible for the final failure. Accordingly, it is not appropriate to apply single phase PtAl2 coating in the high temperature services involving stress and load. The degradation mechanism of the singular PtAl2 coating is investigated by discussing the stress generated from cyclic heating and cooling.

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Oxidation Behavior and Oxide Transformation of a Pt-Modified Aluminide Coating at Moderate High Temperature

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

Effect of pre-oxidation on the failure mechanisms of EB-PVD thermal barrier coatings with (Ni,Pt)Al bond coats

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Failure Behaviors of EB-PVD Thermal Barrier Coatings under Isothermal Oxidation and Thermal Cycling Conditions

High‐temperature oxidation and TGO growth behavior of Sr.9(Zr.9Yb.05Y.05)O2.85 thermal barrier coatings

Oxidation Property and Failure Mechanism of A Single Phase Ptal2 Coating

Modification of NiCoCrAlY with Pt: Part II. Application in TBC with Pure Metastable Tetragonal (t′) Phase YSZ and Thermal Cycling Behavior

Influence of Composition of TGO on the Thermal Shock Lifetime of Thermal Barrier Coatings with Cold-Sprayed MCrAlTaY Bond Coat

Effect of Tensile Load on High Temperature Oxidation of CoNiCrAlY Coating

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

High-temperature Oxidation and TGO Growth Behavior of Sr.9(Zr.9Yb.05Y.05)O2.8 5 Thermal Barrier Coatings

Oxidation Behaviors of the NiCrAlY Bond Coats in the Thermal Barrier Coatings under External Loads

High-temperature oxidation behavior of aluminide coatings on a new cobalt-base superalloy in air