Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Song Peng,Chen Rong,Feng Jing,Lu Jianguo,Lu Jiansheng

DOI: https://doi.org/10.11900/0412.1961.2017.00093

IF: 1.797

2017-01-01

ACTA METALLURGICA SINICA

Abstract:NiPtAl coatings are widely used as overlaying coatings besides bondcoats for thermal barrier coating (TBC) systems within high temperature environment. Oxidaiton behavior of NiPtAl coatings is mainly contribution for the failure of TBC systems or overlaying coatings. An initial oxide layer growth characteristics play a key role in extending lifetime of TBC system or overlaying coatings. In this work, the oxidation experiments of the Pt modified aluminide coating on CMSX-4 Ni-based alloy were carried out at 1150 degrees C for 1 h in 80% Ar+20%O-2. The microstructures of oxide on the NiPtAl coatings are studied by OM, SEM, TEM and Raman spectroscopy. The results indicated that the oxide layer on the NiPtAl coatings included stable and met-stable Al2O3 after 1 h oxidation, and part of spalled oxide layer as well as pores within the oxide layer. The 0.5 mu m thickness whisker-like theta-Al2O3 could form on NiPtAl coating during the initially oxidation stage. At the initial oxidation stage theta-Al2O3 fastly grew which resulted beta-NiAl to gamma'-Ni3Al transformation. The Pt particles formed on the inter-surface between alpha-Al2O3 and theta-Al2O3 layer due to a less Pt solid solubility in gamma'-Ni3Al compared to beta-NiAl in the coating. Fast growth of initial Al2O3 could induce pores formation within the alumina layer. The pores and stress due to oxidation and phase transformation could decrease the alumina adherence, and at last result in the oxide spallation.