Top surface roughness evolution during selective laser melting of AlCu5MnCdVA aluminum alloy

Zhiheng Hu,Yang Qi,Balasubramanian Nagarajan,Xiaojia Nie,Hu Zhang,Haihong Zhu,Xiaoyan Zeng

DOI: https://doi.org/10.1016/j.jmapro.2021.01.051

IF: 5.684

2021-04-01

Journal of Manufacturing Processes

Abstract:<p>Selective laser melting (SLM) is a powder bed based additive manufacturing (AM) technology which is expected to fabricate parts with complex structure. Top surface roughness, a key quality index for SLM which strongly affects the lifetime of the recoater blade, changes due to the complex thermal history during SLM. This paper systematically studied the top surface roughness evolution during selective laser melting (SLM) of an Al-Cu alloy, which is widely employed in aerospace, automotive, and military industries. Single-track, single-layer, multi-layers, and cubic samples were fabricated. The fluid flow intensity affected both the roughness along the scanning direction and the roughness perpendicular to the scanning direction whereas the roughness perpendicular to the scanning direction was also affected by the overlapping of the molten pool. As the layer number increased, the increases in the fluid flow contributed to the spreading of the molten pool. However, the increases in the powder thickness harmed the top surface quality in both directions. Besides, the top surface roughness led to the fluctuation of the powder thickness in the subsequent layer, which resulted in the instability of the molten pool. As a result, for most of the tested processing conditions, an initial increase in the surface roughness was observed followed by a reduction before reaching saturation when the layer number increased. Larger hatch spacing weakened the effect of the thermal accumulations, which reduced the growth rate of the fluid flow intensity and limited the reduction in the surface roughness. This study can bring insights into the understanding of the top surface roughness evolution during SLM.</p>

engineering, manufacturing

What problem does this paper attempt to address?

This paper attempts to solve the problem of the evolution of the top - surface roughness of AlCu5MnCdVA aluminum alloy during the Selective Laser Melting (SLM) process. Specifically, the paper focuses on how to optimize the surface quality of aluminum - copper alloys in the SLM process by systematically studying the influence of different processing parameters on the top - surface roughness. This is not only crucial for improving the overall performance of parts manufactured by SLM technology, but also of great significance for ensuring the stability of the SLM process and the good surface quality of subsequent layers.

The paper mentions that the top - surface roughness is a key quality indicator, which strongly affects the life of coated inserts in the SLM process. Due to the complex thermal history during the SLM process, the top - surface roughness will change. By studying the preparation of single - track, single - layer, multi - layer and cube samples, the author explored the influence of fluid flow intensity on the roughness in the scanning direction and perpendicular to the scanning direction, as well as the influence of molten pool overlap on the roughness perpendicular to the scanning direction. In addition, as the number of layers increases, the change in powder thickness will also affect the top - surface quality. The paper also discussed how these factors cause the surface roughness to increase initially, then decrease, and finally reach a saturation state, especially under different processing conditions. These research results are helpful for understanding the evolution mechanism of the top - surface roughness in the SLM process, thereby providing a theoretical basis for optimizing SLM process parameters.