Abstract:In metal-based additive manufacturing, laser power, scanning speed, hatching distance and layer thickness are important manufacturing parameters. These parameters are very important in terms of microstructure, mechanical properties and surface quality of the final product. For this reason, it is very important choosing these parameters correctly in the production process. One of the common approaches used to optimize these parameters is volumetric energy density. In this study, product quality improvement in additive manufacturing of AlSi10Mg alloy was focused, and test pieces were produced at different volumetric energy densities. The parts were manufactured according to the Taguchi L 9 orthogonal array experimental design. Three different laser powers (250–300–350 W), three different scanning speeds (900–1000–1100 mm/s), three different hatching distances (0.17–0.19–0.21 mm) and constant layer thickness values were used as manufacturing parameters. The performance properties of the manufactured parts were investigated in terms of mechanical properties and surface roughness. As a result of the study, it was observed that the mechanical properties of the samples produced at very high and very low volumetric energy densities decreased and the surface roughness increased. Maximum mechanical properties within the produced samples were obtained at 55.82 J/mm 3 volumetric energy density, and minimum surface roughness was obtained at 54.46 J/mm 3 volumetric energy density. For mechanical properties and surface roughness, multiple response optimization was performed with Taguchi-based Grey relational analysis method. According to the experimental results, optimum manufacturing parameters for additive manufacturing of AlSi10Mg alloy; it was obtained as 350 W laser power, 1100 mm/s scanning speed, 0.19 mm hatching distance and 55.82 J/mm 3 volumetric energy density, which is the interaction of these parameters. The mechanical properties and surface roughness obtained graphically were supported by fracture surface images and microstructure studies. With multiple response optimization, 30.15% improvement was achieved in performance indicators. In addition, it has been demonstrated that volumetric energy density can be used as an important evaluation tool in determining product quality.

An experimental investigation of the influence of SLM input factors on the as-built AlSi10Mg surface quality

An Investigation into the Influence of Processing Parameters on the Surface Quality of AlSi10Mg Parts by SLM Process

Surface texture measurement for additive manufacturing

Experimental Study on Circular Overhang Circularity and Surface Quality in AlSi10Mg Manufactured by Laser Powder Bed Fusion

Experimental and statistical investigation of mechanical properties and surface roughness in additive manufacturing with selective laser melting of AlSi10Mg alloy

Influence of Contour Scan Variation on Surface, Bulk and Mechanical Properties of LPBF-Processed AlSi7Mg0.6

Top surface roughness evolution during selective laser melting of AlCu5MnCdVA aluminum alloy

The Influence of Process Parameters on Vertical Surface Roughness of the AlSi10Mg Parts Fabricated by Selective Laser Melting

Effect of processing parameters on overhanging surface roughness during laser powder bed fusion of AlSi10Mg

Metallurgical Defects and Roughness Investigation in the Laser Powder Bed Fusion Multi-Scanning Strategy of AlSi10Mg Parts

Research and Optimization of Surface Roughness in Milling of SLM Semi-Finished Parts Manufactured by Using the Different Laser Scanning Speed

Experimental Study and Random Forest Machine Learning of Surface Roughness for a Typical Laser Powder Bed Fusion Al Alloy

On the selective laser melting based additive manufacturing of AlSi10Mg: The process parameter investigation through multiphysics simulation and experimental validation

Effects of Building Direction, Process Parameters and Border Scanning on the Mechanical Properties of Laser Powder Bed Fusion AlSi10Mg

Process parameter optimization and mechanical properties for selective laser melting of AlSi10Mg alloy

Direct Metal Laser Sintering to Develop Complex Contours of Aisimg Aluminium Alloy - Build Parameters Optimization

Effect of Selective Laser Melting Process Parameters on the Quality of Al Alloy Parts: Powder Characterization, Density, Surface Roughness, and Dimensional Accuracy

The effect of process parameters and scanning strategies on surface roughness of stainless steel 316L SLM parts

Considerations on the surface roughness of SLM processed metal parts and the effects of subsequent sandblasting

Investigation of the accuracy and roughness in the laser powder bed fusion process

Study on Surface Roughness Improvement of Selective Laser Melted Ti6Al4V Alloy