Abstract:Yttrium silicate (Y2SiO5) is considered as one of the most promising candidate materials for environmental barrier coatings. In this paper, Y2SiO5 powder with a single phase were successfully prepared by high-temperature solid phase reaction method. The influence of sintering behavior on the microstructure, phase composition and mechanical properties of Y2SiO5 ceramics was studied at 1400 °C. In addition, the corrosion behavior and mechanism of Y2SiO5 against CMAS at 1250 °C and 1350 °C were also investigated. The results showed that the grain size of the prepared Y2SiO5 ceramic was about 1.28 µm with relatively uniform, and there were many pore structures. Although Y2SiO5 was still the main phase, a new small amount of Y4.67(SiO4)3O phase was formed in Y2SiO5 ceramics after sintering at 1400 °C for 25 h. The sintering phenomenon of Y2SiO5 ceramics occurred at 1400 °C: the porosity decreased and the grain size grew. With the increase of sintering time, fracture toughness first increased and then decreased. The maximum fracture toughness was 4.84 MPa m1/2 after 50 h sintering. Part of Y2SiO5 was dissolved in CMAS melt and Ca4Y6(SiO4)6O rare-earth oxyapatite phase was generated after CMAS corrosion for 24 h. The corrosion zone could be divided into loose corrosion area (about 93 µm thickness) and dense reaction layer with Ca4Y6(SiO4)6O phase (about 16 µm thickness) at 1250 °C for 24 h. With the increase of corrosion time and corrosion temperature, both the corrosion depth of CMAS and the thickness of dense reaction layer increases. The dense Ca4Y6(SiO4)6O layer can effectively resist the further corrosion of CMAS melt.

In-situ Grown Y3Si2C2 on RB-SiC Ceramic for Enhanced Wet-Oxygen Corrosion Resistance

Microstructure and Wet-Oxygen Corrosion Behaviors of In-Suit Grown Y3Si2C2 Modified SiCf/SiC Composites

Microstructure and corrosion behavior of in-situ grown Y3Si2C2 coated SiC fibers exposed to air and wet-oxygen at 1400 °C

Enhanced wet-oxidation resistance of Y2O3 modified SiC ceramics by the formation of Y2Si2O7 protective layer

Oxidation protection of tri‐layer La2Zr2O7/Yb2Si2O7/SiC‐coated Cf/SiC composites at high temperature

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites

Preparation and properties of SiC/SiC-SiYC with excellent water-oxygen corrosion resistance

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites

Thermal shock behavior and oxidation resistance of novel SiC nanowires+Si/Yb2Si2O7-Si/Yb2Si2O7 environmental barrier coatings

Y/YbB4-modified SiCf/SiC composites with enhanced water-oxygen corrosion resistance

Oxidation resistance and thermal shock behavior of tri-layer Si/Si–Yb2SiO5/Yb2SiO5–SiC environmental barrier coatings at 1300 °C

The Oxidation Behavior and Corrosion Mechanism of SiC Matrix Ceramics in a High Temperature Wet Air Environment

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Thermal aging and CMAS corrosion behaviors of Y2SiO5 ceramic for environmental barrier coatings

Thermal cycling behavior of La2Zr2O7/Yb2Si2O7/SiC coated PIP Cf/SiC composites under burner rig tests

A Novel Design of Oxidation Protective Β-Y 2 Si 2 O 7 Nanowire Toughened Y 2 SiO 5 /Y 2 O 3 -Al 2 O 3 -Sio 2 Glass Ceramic Coating for SiC Coated Carbon/carbon Composites

Preparation of oxidation protective ZrB 2 –SiC coating by in-situ reaction method on SiC-coated carbon/carbon composites

Design and Preparation of an Ultra-High Temperature Ceramic by In-Situ Introduction of Zr2[Al(Si)]4C5 into ZrB2-SiC: Investigation on the Mechanical Properties and Oxidation Behavior

Oxidation properties of tri-layer ytterbium-disilicate/mullite/silicon-carbide environment barrier coatings for Cf/SiC composites

Thermal cycling behavior of bi-layer Yb2Si2O7/SiC EBC-coated Cf/SiC composites in burner rig tests

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites