Abstract:Preparing antioxidant coatings to address the inherent oxidation sensitivity of carbon fiber-reinforced carbon aerogel (C/CA) composites is a feasible way to promote their application in oxidizing environments as thermal insulation materials. However, preparing the coatings with excellent oxidation and ablation resistance while avoiding evident damage to the C/CA substrate still remains a challenge. Herein, a SiC@SiO2 nanowire-toughened ZrB2-SiC/SiC bilayer coating with a large thickness of 500 mu m was prepared on C/CA using a one-step low-temperature reaction sintering method, which simultaneously formed a sintered outer layer with even-distributed nanowires and a siliconized gradient inner layer. By courtesy of the synergic thermal response of the layers and the crack deflection induced by the nanowires, the resulting coating has moderate residual compressive stress of 0.08-1.22 GPa in the interface, high interfacial bonding strength of 6.02 MPa, and good fracture toughness of 4.36 MPam1/2. Benefited from the optimum components and improved structure, the coating shows excellent cyclic ablation resistance with linear ablation rates of 0.1 mu m/s at 1650 degrees C for 1500 s (300 s x 5 cycles) and 0.4 mu m/s at 1850 degrees C for 900 s (300 s x 3 cycles). The one-step preparation strategy contributes to little damage to the substrate, thus showing the well-preserved mechanical and thermal insulation properties.

Preparation of oxidation protective ZrB 2 –SiC coating by in-situ reaction method on SiC-coated carbon/carbon composites

Oxidation Protection and Behavior of In-Situ Zirconium Diboride–silicon Carbide Coating for Carbon/carbon Composites

ZrB2–SiC Gradient Oxidation Protective Coating for Carbon/carbon Composites

Ultra-high Temperature Ceramic TaB2–TaC–SiC Coating for Oxidation Protection of SiC-coated Carbon/carbon Composites

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

Preparation of a multi-composition coating for oxidation protection of modified carbon-bonded carbon fiber composites by a rapid sintering method

Design and Preparation of an Ultra-High Temperature Ceramic by In-Situ Introduction of Zr2[Al(Si)]4C5 into ZrB2-SiC: Investigation on the Mechanical Properties and Oxidation Behavior

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

ZrSi2-SiC/SiC Anti-Oxidant Coatings Prepared on Graphite Spheres by Two-Step Pack Cementation Process

Oxidation Protection Of Zrb2-Sic Modified Carbon-Bonded Carbon Fiber Composites

Using in-situ conversed nano SiC to bond UHTC particles and construct anti-ablation coating

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Oxidation protection of tri‐layer La2Zr2O7/Yb2Si2O7/SiC‐coated Cf/SiC composites at high temperature

Facile Preparation of a SiC@SiO2 Nanowire-Toughened ZrB2–SiC/SiC Bilayer Coating with Good Interfacial Bonding, High Toughness, and Excellent Cyclic Ablation Resistance on C/CA Composites

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites