Α-Lamella Orientation Dependence of Fatigue Crack Propagation in As-Forged TiB/near Α-Ti Composite

Fanchao Meng,Rui Zhang,Shuai Wang,Fengbo Sun,Ming Ji,Cunyu Wang,Lujun Huang,Lin Geng
DOI: https://doi.org/10.1016/j.ijfatigue.2024.108610
IF: 5.489
2025-01-01
International Journal of Fatigue
Abstract:The influence of microstructural attributes on fatigue crack propagation in titanium matrix composite remains largely unexplored. The impact of alpha-lamella crystallographic and spatial orientations on fatigue crack propagation in an as-forged TiB/near alpha-Ti composite was investigated using innovative quantitative tilt fractography and electron backscattered diffraction techniques. Crack initiation was observed from TiB cluster defects, followed by faceted fatigue crack propagation across alpha lamellae. In long-life failure, facet formation appears to be driven by a combination of slip and resolved normal stress across the facet plane, with facet angles relative to the loading direction (LD) predominantly ranging between 30.0 degrees and 50.0 degrees. In contrast, short-life failure exhibited shear deformation as the primary mode, with facet angles relative to LD mainly between 40.0 degrees and 50.0 degrees. Crystallographic orientation analysis revealed that facets predominantly formed near the basal plane in both long-life and short-life failures. Crack-initiation microstructural neighborhoods favoring basal slip increased effective slip length over alpha lamellae, reducing resistance to crack propagation. This led to a rise in basal geometrically necessary dislocation (GND) density from 1.2 x 10(13) m(-2) in long-life to 3.6 x 10(13) m(-2) in short-life failures. These observations highlight the dominance of spatial and crystallographic orientations of alpha lamellae in controlling fatigue crack propagation.
What problem does this paper attempt to address?