Influence of microstructure on fatigue crack growth behavior of Ti–6Al–3Nb–2Zr–1Mo alloy: Bimodal vs. lamellar structures

Junqiang Ren,Qi Wang,Binbin Zhang,Dan Yang,Xuefeng Lu,Xiaobo Zhang,Xudong Zhang,Jingyu Hu

DOI: https://doi.org/10.1016/j.intermet.2020.107058

IF: 4.075

2021-03-01

Intermetallics

Abstract:<p>The influence of microstructure (bimodal and lamellar structure) on the fatigue crack growth (FCG) rate of Ti–6Al–3Nb–2Zr–1Mo alloy was investigated using compact-tension (CT) specimens. The da/dN curves showed that the FCG rate of lamellar structure was slower than that of bimodal structure, especially in the early stage of crack growth. The FCG paths in the early stage were observed by optical microscopy and scan electric microscopy. The results revealed that the FCG paths of lamellar structure were more tortuous than that of bimodal structure. The frequency of crack deflection and bifurcation of the lamellar structure is significantly higher than that of bimodal structure. The dominant mode of crack propagation for bimodal structure is crossing βtrans and αp, and for lamellar structure is crossing α colonies. Fatigue crack growth mechanisms at the early stage have been studied by observation of crystalline orientation near the crack propagation path at the crack tip, in combination with the slip trace analyzing. The results show that the fatigue crack growth directions in αp or βtrans for bimodal structure and α colony for lamellar structure are mostly consistent with that of prismatic or basal plane trace. This indicated that the cracks propagation modes of crossing αp or βtrans in bimodal structure and crossing α colonies in lamellar structure are resulting from the slip band cracking of the microstructure at crack tip, as the evidence of <span class="math"><math>{101‾0}112‾0</math></span> prismatic dislocation lines were observed in αp or βtrans for bimodal structure and α colony for lamellar structure by transmission electron microscope (TEM) near the fracture surface.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering