Abstract:The influence of orientation on the creep rupture properties of a single crystal superalloy DD6 under multiaxial stress was carried out at 980 degrees C and 400 MPa. A circumferential V-type notched specimen had been designed to investigate the effect of multiaxial stress state on the creep behavior. It was found that the creep lifetimes of the [111] oriented notched specimen were slightly longer than that of the [011] orientation and 1.36 times longer than that of the [001] orientation. The computational results showed that the strain and damage distribution revealed fourfold symmetry, double symmetry and threefold symmetry for [001], [011] and [111] orientation respectively, which was confirmed by experimental observation. At high temperature the creep anisotropy in three different orientations exhibited mainly in primary and secondary creep stages. Through the study of notched specimens by SEM, the morphology evolution of gamma'-phase proved that the directional coarsening was strongly dependent on the local effective stress and the direction of the local max principal stress with respect to loading axis. Fracture morphology displayed uneven cleavage configuration with multi-level feature, and the cleavage planes parallels (001), (011) and (111) crystal plane for [001], [011] and [111] orientation, respectively. The cleavage plane, which is attributed to the cracks propagated along the interfaces of gamma/gamma'phases, displayed square-like, rhombus-like and hexagon-like feature for [001], [011] and [111] orientation, respectively. Due to the higher density in dislocations of {111} planes, it is more easily as the secondary crack when the crack reach the {111} planes, which is thought to be the main reason of forming different feature on primary cleavage plane. (C) 2016 Elsevier B.V. All rights reserved.

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy

Creep-fatigue Behavior of Nickel-Based Single Crystal Superalloy with Different Orientations: Experimental Characterization and Multi-Scale Simulation

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Effects of Crystal Orientations on the Low-Cycle Fatigue of a Single-Crystal Nickel-Based Superalloy at 980 °C

Microstructure Characterization and Damage Coupled Constitutive Modeling of Nickel-Based Single-Crystal Alloy with Different Orientations

Anisotropic Creep Damage and Fracture Mechanism of Nickel-Base Single Crystal Superalloy under Multiaxial Stress

Crack propagation paths and fracture of Ni-based single crystal

Transient Thermal Fatigue Crack Propagation Behavior of a Nickel-Based Single-Crystal Superalloy

Effect of Orientation Deviation on Random Vibration Fatigue Behavior of Nickel Based Single Crystal Superalloy

Effects of secondary orientation on fatigue crack initiation in a single crystal superalloy

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

The effect of crystal orientation on fretting fatigue crack formation in Ni-based single-crystal superalloys: In-situ SEM observation and crystal plasticity finite element simulation

Fracture Behaviour of Compact Tension Specimens of Nickel-based Single Crystal Under Tension Creep and Cyclic Loading

In-situ SEM study of slip-controlled short-crack growth in single-crystal nickel superalloy

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy