Abstract:Total strain-control, low-cycle fatigue experiments of a fourth-generation Ni-based single-crystal superalloy were performed at 980 °C. Scanning electron microscopy and transmission electron microscopy are employed to determine fracture morphologies and dislocation characteristics of the samples. As the strain amplitude increased from 0.6 to 1.0%, the cyclic stress and plastic strain per cycle increased, the cyclic lifetime decreased, more interfacial dislocation networks were formed, and the formation rate accelerated. Cyclic hardening is associated with the reaction of accumulated dislocations and dislocation networks, which hinder the movement of dislocations. The presence of interfacial dislocations reduces the lattice mismatch between the γ and γ′ phases, and the presence of dislocation networks that absorb mobile dislocations results in cyclic softening. At a strain amplitude of 1.0%, the reaction of a high density of dislocations results in initial cyclic hardening, and the dislocation cutting into the γ′ phase is one of the reasons for cyclic softening. The crack initiation site changed from a near-surface defect to a surface defect when the strain amplitude increased from 0.6 to 0.8 to 1.0%. The number of secondary cracks initiated from the micropores decreased during the growth stage as the strain amplitude increased.

Effects of secondary orientation on fatigue crack initiation in a single crystal superalloy

Effects of Secondary Orientation on Crack Closure Behavior of Nickel-Based Single Crystal Superalloys

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

In-Situ Sem Observation and Crystal Plasticity Finite Element Simulation of Fretting Fatigue Crack Formation in Ni-Base Single-Crystal Superalloys

In-situ Observations of the Effects of Orientation and Carbide on Low Cycle Fatigue Crack Propagation in a Single Crystal Superalloy

Crystal Orientation Effect on Fretting Fatigue Induced Geometrically Necessary Dislocation Distribution in Ni-based Single-Crystal Superalloys

Effects of secondary orientations on long fatigue crack growth in a single crystal superalloy

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Secondary orientation effects on the low cycle fatigue behaviors of rectangular‐sectional Ni‐based single crystal superalloys at medium and high temperatures

Effects of secondary orientation and temperature on the fretting fatigue behaviors of Ni-based single crystal superalloys

In-situ SEM study of slip-controlled short-crack growth in single-crystal nickel superalloy

Near-threshold fatigue crack propagation in a Ni-based single crystal superalloy affected by crystallographic anisotropy

High temperature in-situ SEM observation and crystal plasticity simulation on fretting fatigue of Ni-based single crystal superalloys

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

Crystallographic analysis on small fatigue crack propagation behaviour of a nickel‐based single crystal superalloy

Fatigue Fracture Mechanism of a Nickel-Based Single Crystal Superalloy with Partially Recrystallized Grains at 550 C by In Situ SEM Studies

Effect of orientations on in situ tensile deformation and fracture behaviours of nickel-base single-crystal superalloys

Effect of local anisotropy on fatigue crack initiation in a coarse grained nickel-base superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Influence of crystal orientations on the creep fracture of a nickel-based single crystal superalloy

Effects of Crystal Orientation and External Stress on the Static Recrystallization Behavior of an Ni-Based Single-Crystal Superalloy